稀土金属Eu掺杂MgF2Microsoft Word 文档.docVIP

稀土金属Eu掺杂MgF2第一性原理研究 姚茂波 （铜仁学院物理与电子科学系2007级1班） 指导老师 李宗宝+ 摘要：运用密度泛函理论（DFT）的第一性原理平面波超软赝势方法和CASTEP软件，计算Eu掺杂MgF2晶体的几何结构，电子结构和光学性质。结果表明，Eu掺杂体系无结构畸变体积会有所增加；导带、价带都发生明显下移，禁带宽度减小不明显，但出现了杂质能级，使得掺杂后的MgF2发生可见光化；其光学性质表明E掺杂对光吸收系数有重要的调制作用。揭示了Eu：MgF2体系在光学元器件方面的潜在应用。 关键词：密度泛函数理论(DFT)，第一性原理，超软赝势，Eu掺杂MgF2 [中图分类号]O471;O641;O649 [学科代码]430.10 [文献标识码]A First-principles study of MgF2 doped with rare earth metal Eu 显示对应的拉丁字符的拼音 ? 字典 - 查看字典详细内容 M.B.Yao,Z.B.Li+ Abstract: By using the plane wave ultrasoft pseudopotential method based on the first-principles of density functional theory (DFT) and CASTEP software, obtained the geometric structure, electronic structure and optical properties of Eu doped with MgF2 crystals. The results showed that the volume will increase; by the time Eu doped system does not have structural aberrations, conduction band and valence band are obviously down, the decrease of forbidden band is not obvious. But impurity level has appeared, making the doped MgF2 occurred under visible light; its optical properties show that the doped Em plays an important role in modulation of light absorption coefficient. Reveals the Eu: MgF2 system in terms of the potential applications of optical components.Key words: density functional theory (DFT), first-principles, ultrasoft pseudopotential, Eu doped MgF2 1．引言 氟化镁（MgF2）是一种无色四方晶体或粉末状，在光电加热下呈弱紫色荧光，其晶体有良好的偏振作用，特别适用于紫外线和红外光谱。用作冶炼金属镁时的溶剂、电解铝的添加剂、光学透镜镀膜、钛颜料的涂着剂、阴极射线屏的荧光材料 [1]。是一种重要的固体激光器发光介质，可制作光学棱镜，透镜和窗口等光学元件。尺寸大的紫外级氟化镁单晶可用于光通讯系统及军工领域[2]。随着光学镀膜材料的开发利用进一步成熟，氟化镁镀膜材料已被应用在纸币的防伪技术。热压多晶氟化镁常用着振流罩材料[3]。作为非常规催化剂载体，也使氟化镁成为人们关注的研究对象[4]。氟化镁在较宽的频率范围内有很高的透过率，在600—1300cm范围内没有特征吸收带，方便用多种测试方法分析所承载的氧化物催化剂的结构。同时，氟化镁载体可以阻止氟氯化碳的液态脱氯作用，可以使催化过程的选择性得到更好的控制。此外，在环保方面，氟化镁可以使有机化合物的液态脱硫、消除氧化氮以及以及催化氧化一氧化碳等方面的催化剂获得很好的催化活性。因此，氟化镁及相关材料在很大程度上受到人们的普片关注[5,6]。 为调控和利用其优异的性能，氟化镁的调制掺杂也开始受到人们的关注，例如，Welford[7]等报道了从1160μm到2130μm和从1175μm到2150μm连续调谐的脉冲激光输出，其中包括峰值1193μm为人体组织所吸收的谱带，该波长激光对人体组织的穿透深度浅、定位精确、损伤小，在临床治疗中