毛用活性低温染料黑WD代替媒介黑PV染色生产工艺.doc

毛用活性低温染料黑WD代替媒介黑PV染色生产工艺 高志国 郭永平 （宁夏荣昌绒业集团有限公司） （Gao zhi guo Guo yong ping） (Ningxia Rongchang Cashmere Group Co,Ltd) 摘要：本文通过试验对毛用活性低温染料染色工艺的研究，最后得出适合羊绒染色的最优工艺路线和最优工艺参数。常规黑PV染色时虽是在弱酸浴中正常沸煮，仍会对纤维造成损伤，断裂强力降低。采用毛用活性低温黑WD染料染色时,染色温度降低,染色时间缩短,而且降低,。Abstract: Through test on low temperature dyeing process of wool with reactive research，finally obtains the optimal for cashmere dyeing process route and optimal process parameters. Conventional dyeing is in weak acid bath for normal boiling, still the fibers will cause damage, breakage strength reduction. With wool reactive dye dyeing at low temperature, lowering temperature, dyeing time, and the damage to the fibers spinnability improved, and can save energy, improve spinning performance and finished handle. After control of the PH, temperature, time, achieve the best dyeing effect. Key words: cashmere、process 、Low- temperature dyes 1 引言 山羊绒是世界上最珍贵的动物纤维，被世界公认为“软黄金”，其制品手感柔软、滑糯、风格典雅、细腻、光泽柔和、亮丽。 染色时，染料向羊绒纤维内部扩散有两种途径: 1)直接通过鳞片层细胞向羊绒内部扩散； 2)通过鳞片细胞间的细胞间隙沿CMC 扩散。 活性染料在羊绒染色中的原理为：吸附、扩散、固着。首先，活性染料母体上所具有的共轭双键、极性基、同平面性的芳环结构以及水溶性基团等，在酸性溶液中迅速地为羊绒所吸收。由于纤维表面吸附了大量染料离子，形成了很高的浓度梯度，促使染料向纤维内部扩散。染料先扩散进入角质层的区域，然后再进入内表皮层的非角阮区，再进入细胞间胶粘物部分。当染色继续进行时，染料渗透入整个非角朊网状结构中而同时从内表皮转移到富含硫的外表皮。最后，染料积聚在纤维富含有胱氨酸的基质及外表皮区域，与羊绒中的胱氨酸水解形成的巯基、赖氨酸的末端氨基、组氨酸中的亚氨基等在弱酸性条件下进行反应，与丝氨酸和苏氨酸的羟基在弱碱性条件下进行反应。其反应性:巯基氨基和亚氨基羟基。[1] 3.2 温度对染色的影响 羊绒纤维在60℃以下时膨化度很小，在表面角质膨化之前，对分子量很小的酸的吸收、扩散都有很大阻力。另外，染料分子动能也发生变化，染料的染色速率也随着发生变化。温度越高，羊绒鳞片层膨化度大，染料的分子动能也会相应的提高，都有利于提高染料的上染率，但染色过程中温度升高不易过快，不然会引起上染过快，容易染花。[2] 本实验控制升温为1℃/min 3.3 pH 对染色的影响 1) 在酸性条件下(低于羊绒等电点) NH3-W-COOH + D-SO3 D-SO3-NH3-W-COOH (羊绒纤维) （染料阴离子） 在低于羊绒等电点的酸性染浴中，羊绒纤维首先吸附氢离子而形成氨基正离子(-NH3+)，因而对染料阴离子及某些阴离子助剂产生吸附，随着染色体系中染料浓度的增加，酸用量的增加pH 值的下降，羊绒纤维对染料阴离子的吸附量增加。 2)在碱性条件下(高于羊绒等电点) NH2-W-COO- D-SO3- NH2-W-COO- ←→-O3S-D 斥力 在碱性条件下，羊绒纤维对染料阴离子的吸附仅靠亲和力的作用。 从上述可以看出，加入酸将增加羊绒纤维表面的正电性，因此，在