气门油封的评价.docVIP

气门油封的评价（试验）设备及评价（试验）条件 The evaluation of valve seal’s test equipment and its condition 一、电脑硫化测试仪(GT-M2000) Computer vulcanization tester(GT-M2000) 用途：用于分析、测定橡胶硫化过程的焦烧时间、正硫化时间、硫化速率、粘弹性模量以及硫化平坦期等性能指标。 Application: in the rubber vulcanization, use to analysis and test some properties such as Scorch time, Vulcanization time, Cure rate, viscoelastic modulus, Curing period flat and so on. 原理：测定胶料在硫化过程中剪切模量的变化，而剪切模量与交联密度成正比，因此测定结果反映了胶料在硫化过程中交联程度的变化，可以测出胶料初始黏度、焦烧时间、硫化速度、正硫化时间和过硫返原性等重要参数。 Principle: in the rubber vulcanization, determine the change of shear modulus; according to shear modulus and crosslinking density have proportional relationship, so test result can reflect the change of crosslinking density of vulcanization. We can easily get some mainly parameter such as initial viscosity, scorch time, cure rate, vulcanization time and reversion of vulcanization. 执行标准：GB/T16584-1996 Execute standard: GB/T16584-1996 系统参数 System parameter: A．测温范围：0℃－200℃ Temperature range: 0℃－200℃ B．测温精度：≤ ±0.3℃ Temperature precision: ±0.3℃ C．控温精度：≤ ±0.3℃ Preciosity of temperature control: ±0.3℃ D．温度分辨率：0.1℃ Temperature distinguishability: 0.1℃ E．力矩量程：0－10N.m 0－20N.m Moment span: 0 to 10N.m 0 to 20N.m F．力矩解析度：0.001N.m Moment resolution: 0.001N.m G．模腔频率：1.7Hz Die cavity frequency: 1.7Hz H．振幅：±0.5o ±1o Amplitude: ±0.5o ±1o I. 环境温度：0－35℃ 相对湿度80％ Environmental temperature:0 to 35℃ J．硫化时间设定范围：2－300min Cure time setting range: 2 to 300min K．配气:0.5MPa Air distributing: 0.5MPa L．电源:交流220V 800W Power: AC 220V 800W 二、A型邵氏硬度计Application: apply to test the hardness of middle-low hardness plastic, rubber, multiple lipid, leather and wax. 原理：在试验力作用下垂直压入试样表面，当压足表面与试样表面完全贴合时，压针尖端面相对压足平面有一定的伸出长度L，以L值的大小来表征邵氏硬度的大小，L值越大，表示邵尔硬度越低，反之越高。 Principle: in the test, vertical pressure to the sample surface, when the contact foot and sample surface completely joint, contact tip has a certain extension length L relative to contact foot. So use L calculation the shore hardness, if L is greater that the lower Shore har