金属基底上薄膜力学性能测试方法I：弹性膜（可编辑）.doc

金属基底上薄膜力学性能测试方法I：弹性膜  5 10 15 20 （北京科技大学腐蚀与防护中心环境断裂重点实验室，北京 100083） 摘要：本文利用金属材料在往复变形过程中流变应力不变的原理，提出了通过带膜和无膜试 样屈服应力和流变应力差值法测量金属基底上薄膜残余应力的方法，并用有限元模拟检验了 该方法的有效性。通过实验测量了黄铜在 Mattsson 溶液中形成的腐蚀产物膜的残余应力， 检验了所提出方法的一致性。 关键词：有限元；残余应力；腐蚀产物膜；电镀膜 中图分类号：TG172.9 A novel method to measure the mechanical properties in a corrosion film formed on metallic substrates I: Elastic film YUAN Wenjuan, SU Yanjing Corrosion and Protection Center Key Laboratory for Environmental Fracture MOE , University of Science and Technology Beijing, Beijing 100083 Abstract: This paper theoretically proposed a series of formulae for a novel tensile testing method to extract the residual stress in the surface film on metallic substrates. Finite element calculations were conducted to verify the accuracy and reliability of the proposed formulae. From the tensile stress-strain curves of metallic substrates with and without a surface film, one can evaluate the residual stress in the film using these formulae. A tarnish film on a brass substrate formed after immersion in Mattsson’s solution was tested to demonstrate these methods. Keywords: Finite element method; residual stress; corrosion product films; electrodeposition film 25 0 引言 薄膜残余应力是影响薄膜力学性能的重要参量。因此，人们发展了许多测量薄膜残余应 力的实验方法，包括 X 射线衍射和电子衍射技术[1-3]，以及弯曲实验方法[4-6]等。但这两种方 法有一定的局限性和误差，因此需要一个新方法来测量膜内的残余应力。 30 金属中塑性变形是通过位错的运动进行的。当外应力大于材料的屈服强度时，位错形成 并且运动，从而发生永久性的塑性变形。位错密度随材料外加应力的增大而增大[7]，导致材 料的应变硬化现象。颈缩前，金属的塑性应变（ f ）与流变应力（? f ）之间的关系可以表 示为： ? f K? n  1 35 式中 K 为强度系数；n 为应变硬化指数。 根据公式（1）可以看出，金属材料的流变应力只与塑性应变有关。金属材料加载至超 过屈服强度? Y 后卸载，则原子键恢复到初始状态，但是仍留有塑性应变，如图 1 所示。因 此，卸载过程中对应于流变应力 f 的总应变为 f pl el （ el ? f E ，E 为杨氏 模量）。当试样再次加载时，只有当外加应力达到卸载时的流变应力时，位错才再次运动。 基金项目：高等学校博士学科点专项科研基金资助课题（20090006110011） 作者简介：原文娟，（1983-），女，博士研究生，主要从事材料力学性能和应力腐蚀的研究。 通信联系人：宿彦京，（1965-），男，教授，主要从事应力腐蚀和氢脆方面的研究。E-mail: yjsu@ -1-  40 45 50 55  在反复加载-卸载的过程中，应力应变曲线也符合上述规律，如图 1（a）所示。 图 1 （a）H62 黄铜加载-卸载循环的应力应变曲线;（b）带膜与无膜 H62 黄铜的应力应变曲线 Fig.1 The stress-strain curves fo