协同钝化技术在镀锌钢板表面应用.docVIP

协同钝化技术在镀锌钢板表面应用 　　摘要: 协同钝化技术是防腐蚀领域重要的应用技术之一，许多高效的复合缓蚀剂是根据协同效应原理研制的.协同效应不是几种缓蚀剂的简单加和，而是相互促进的结果.协同技术因能够充分地发挥各种缓蚀剂的作用，在防腐蚀领域被广泛采用.简要综述了常规无机-有机缓蚀剂协同作用及有机缓蚀剂的选用原则. 　　? 　　关键词: 协同钝化；成膜机理；选用原则? 　　中图分类号:TG 174.4 文献标志码:A 文章编号:1672-8513(2011)05-0313-04 　　 　　Application of Collaborative Passivation for Galvanized Surfaces 　　 　　ZHANG Ying?jie??1,2?,FANG Zhi?ling?2, DONG Peng?2, LIU Cheng?hui?2 　　? 　　 　　 (1. Key Lab of Ethnic Medicine Resource Chemistry，State Ethnic Affairs Commission Ministry of Education，?Yunnan University of Nationalities, Kunming 650031, China；?2. Faculty of Metallurgical and Energy Engineering，Kunming University of Science and Technology，Kunming 650093，China) 　　 　　Abstract: 　　 　　Synergistic anti-corrosion passivation is one important application technology in the anticorrosion field, and the developments of many efficient corrosion inhibitors are based on the principle of synergy. Synergy is not only a simple addition of corrosion inhibitor, but also a mutually reinforcing result. Synergistic anti-corrosion passivation fully plays the role of various inhibitors, widely used in the field of corrosion. General organic-inorganic corrosion inhibition and synergistic effect of organic inhibitor selection principle are the focus of this study. 　　? 　　Key words: 　　synergistic anti-corrosion passivation；formation mechanism；principle for application 　　 　　镀锌是钢铁领域重要的防腐技术之一，镀锌钢板因其具有良好的防腐蚀性能而被广泛地用于汽车、家电、建筑和航空等领域.但镀锌钢板在潮湿的环境中易被腐蚀，产生白色的腐蚀产物，严重影响镀锌钢板的防腐蚀能力.在镀锌钢板表面采用铬酸盐钝化技术可以大大提高镀锌钢板的防腐蚀能力，并且铬酸盐钝化技术工艺简单、成本低廉.但铬有剧毒，对人体健康和环境造成了严重的危害.协同钝化技术是无铬、环境友好型钝化技术，2003年Ferreira等［1］利用稀土铈及镧离子与硅烷之间的协同作用在镀锌钢板表面制备稀土-硅烷复合膜，结果发现协同钝化技术产生的复合膜的耐腐蚀性比单一膜层要优良得多.随后有大量的研究者将协同钝化技术应用于镀锌钢板防腐蚀领域，本文主要阐述无机-有机缓蚀剂的协同钝化效应在镀锌钢板表面的应用. ? 　　1 无机-有机缓蚀剂协同钝化技术? 　　2001年Aramaki［2］研究了以硝酸铈与Na?2Si??x?O?5作为缓蚀剂在镀锌层表面生成有机硅氧络合物复合膜在0.5 M NaCl中的修复性，实验采用2步钝化法，第1步将试样经??0.015?2??mg/cm?2 Ce(NO?3)?3溶液处理在其表面生成稀土转化膜，后在90?℃下干燥1?h，第2步将经过第1步处理后的试样再经过乙醇和Na?2Si??x?O?5混合溶液处理，然后在90?℃下干燥??22?h?.随后通过电化学测试技术分析复合膜的循环伏安曲线，且通过