应用电化学论文.doc

电化学腐蚀原理和现实生产生活上的应用 摘要：腐蚀现象都是由于金属与一种电解质（水溶液或熔盐）接触，因此有可能在金属／电解质界面发生阳极溶解过程（氧化）。这时如果界面上有相应的阴极还原过程配合，则电解质起离子导体的作用，金属本身则为电子导体，因此就构成了一种自发电池，使金属的阳极溶解持续进行，产生腐蚀现象。 关键词：电化学腐蚀原理；晶间腐蚀；均匀腐蚀；应力腐蚀；防护与应用；镀层；阳极保护 Electrochemical corrosion principle and practical application of production and life Summary: Decay phenomena to all contact a kind of electrolyte(aqueous solution or Rong salt) because of metal, therefore probably take place in metal/electrolyte interface anode deliquescence process.(oxidize)At this time if there is homologous cathode on the interface restoring a process match, the electrolyte then contains the function of ion conductor, metal then is electronics conductor, therefore constituted a kind of self-moving battery, make the metal anode deliquescence keeps on carrying on, the creation decays a phenomenon. Keyword: Electrochemical corrosion principle；Intergranular corrosion；Uniform corrosion；Stress corrosion；Protection and application；coating；Anode protection 随着社会生产力的发展，人民生活水平的提高，金属的使用在日常生活中应用的越来越普遍，由金属腐蚀所带来的损失也越来越严重，这样研究金属的腐蚀与防护便显得非常的重要，本论文主要综合讲述了金属的电化学腐蚀的基本原理和分类，以及讨论了有关现实生产生活中具体的防护措施，以更好的指导现实实践。 电化学腐蚀原理 金属表面由于外界介质的化学或电化学作用而造成的变质及损坏的现象或过程称为腐蚀。介质中被还原物质的粒子在与金属表面碰撞时取得金属原子的价电子而被还原，与失去价电子的被氧化的金属“就地”形成腐蚀产物覆盖在金属表面上，这样一种腐蚀过程称为化学腐蚀。由于金属是电子的良导体，如果介质是离子导体的话，金属被氧化与介质中被还原的物质获得电子这两个过程可以同时在金属表面的不同部位进行。金属被氧化成为正价离子（包括配合离子）进入介质或成为难溶化合物（一般是金属的氧化物或含水氧化物或金属盐）留在金属表面。这个过程是一个电极反应过程，叫做阳极反应过程。被氧化的金属所失去的电子通过作为电子良导体的金属材料本身流向金属表面的另一部位，在那里由介质中被还原的物质所接受，使它的价态降低，这是阴极反应过程。在金属腐蚀学中，习惯地把介质中接受金属材料中的电子而被还原的物质叫做去极化剂。经这种途径进行的腐蚀过程，称为电化学腐蚀。在腐蚀作用中最为严重的是电化学腐蚀，它只有在介质中是离子导体时才能发生。即便是纯水，也具有离子导体的性质。在水溶液中的腐蚀，最常见的去极化剂是溶于水中的氧(O2)。例如在常温下的中性溶液中，钢铁的腐蚀一般是以氧为去极化剂进行的： 如果氧供应充分的话，Fe(OH)2：还会逐步被氧化成含水的四氧化三铁Fe3O4·mH2O和含水的三氧化二铁Fe2O3·nH2O。钢铁在大气中生锈，就是一个以O2为去极化剂的电化学腐蚀过程，直接与金属表面接触的离子导体介质是凝聚在金属表面上的水膜，而最后形成的铁锈是成分很复杂的铁的含水氧化物，有时还有一些含水的铁盐。一般氧最易到达铁锈的最外层，其中铁是三价；铁锈最里层，铁是二价；中间层有可能是含水的四氧化三铁。 在水溶液中电化学腐蚀过程的另一个重要的去极化剂是H+。在常温下，对铁而言，在酸性溶液中可以以H十离子为去极化剂而腐蚀，其过程是： 阳极： Fe-Fe2+ +2e 阴极： 2H++2eH2 总的反应： Fe+2H+Fe2++H2 故此时腐蚀反应产物是氢气和留在溶液中的二价铁离子。