几种单体助磨剂对水泥性能影响 　　中图分类号：TV42+1文献标识码： A 文章编号： 　　摘 要： 对四种单体水泥助磨剂进行了助磨效果和对水泥常规物理性能影响的研究。试验表明，这几种单体助磨剂都有较好的助磨效果又能改善水泥的部分性能，尤其能改善水泥的颗粒分布，具有明显提高水泥强度的作用。助磨效果以三乙醇胺和三异丙醇胺最好，对28d强度增进最明显的是三异丙醇胺。几种单体助磨剂对凝结时间基本没有影响，但是对水泥胶砂干缩有不同程度的不利影响。 　　关键词： 助磨剂；助磨效果；水泥性能 　　Abstract：Grinding effect and effect of cement property on four monomer cement grinding aids were studied. Tests showed that these types of monomers grinding aids have a good grinding effect of cement and also can improve some of the performance, In particular, they all can improve the particle size distribution of cement, then markedly improved the impressive strength of cement. Triethanolamine and triisopropanolamine have better grinding effect, and triisopropanolamine promote the most obvious impressive strength of the 28d . Grinding Aids on the setting time of several monomer had no effect, but shrinkage of cement mortar have an adverse effect. 　　Key words：cement grinding aids；grinding effect；cement property 　　中图分类号：TQ 172.4+63 　　在美国和日本，95%以上的水泥厂使用水泥助磨剂，而在我国，其使用率不到30%。虽然关于水泥助磨剂作用机理的研究还不够深入，使用中存在很多问题有待解决，但水泥助磨剂的作用已被公认，其使用也越来越受到广泛的重视，水泥助磨剂具有广阔的应用前景。生产实践表明，同一助磨剂对不同水泥的助磨作用差异很大，而不同助磨剂对同一水泥的助磨作用也不尽相同。为此，选择了几种不同单体助磨剂对普通硅酸盐水泥进行了一系列的试验研究，以寻求相关的使用规律，为正确使用助磨剂、助磨剂的开发研究提供可靠的依据。 　　1.试验 　　1.1 主要原料 　　熟料：化学成分及矿物质量组成见表1 　　 　　 　　助磨剂：乙二醇(EG)、三乙醇胺(TEA)、三异丙醇胺(TIPA)、木质素磺酸钙（化学分析纯） 　　二水石膏 　　1.2 试验依据和方法 　　配料5kg，其组成为熟料95%，石膏5%.将水泥熟料和石膏破碎至小于7mm大于1mm后入磨，助磨剂配成一定的浓度在入磨前滴加。粉磨设备为φ500mm×500mm试验磨，掺与不掺助磨剂粉磨时间相同，均为26min。粉磨后进行粉体特性测试和水泥性能测试。水泥比表面积参照GB8074，水泥标准稠度用水量、凝结时间测定依据GB 1346，水泥胶砂强度试验依据GB 17671，水泥胶砂干缩依据 JC/T 603，水泥粒度分布用激光粒度分析仪测定。 　　2. 试验结果及分析 　　为了对水泥助磨剂的使用有一个更加直观的认识，对水泥助磨剂的几种不同掺量分别进行了系统的研究。 　　2.1 助磨剂的助磨效果试验结果及分析 　　2.1.1 助磨剂对比表面积的影响 　　由于细度只表示了粗颗粒的含量，而细颗粒的含量及各粒径颗粒的比例均不得而知。因而不能完全用细度表示助磨剂的助磨效果。勃氏比表面积虽然较细度有所进步，但仍然不是一个精确的指标，不能反映水泥分散度的全部指标。具有相同的比表面积，可能具有大的平均粒径和宽的粒径分布，也可能具有小的平均粒径和窄的粒度分布[1]。所以，对水泥助磨剂的效果以细度和比表面积只能进行粗略比较，深入详细的比较应以水泥的粒度分析为准。本文采用勃氏比表面积和颗粒分布来讨论助磨的助磨效果。助磨剂的助磨效果见表2 　　 　　 　　由表2可以看出，各种助磨剂的助磨效果有差别。乙二醇和三异丙醇胺的助磨效果最好，三乙醇胺次之，木质素磺酸钙的助磨效果不