混凝土裂缝成因以及预防措施.docVIP

混凝土裂缝成因以及预防措施 　　 摘要：混凝土在现代城市建设中具有重要的位置，但是伴随这类材料的应用越来越广泛，混凝土结构的裂缝问题也开始日益受到人们的关注。混凝土结构的裂缝不但会影响结构的美观，也会影响结构的耐久性和使用年限。当裂缝达到一定宽度的时候，就可能危及建筑的安全。大量科研和实践证明了出现裂缝是混凝土不可避免的问题，但科学的要求是通过一定方法将其有害程度控制在适当范围内。 　　关键词：混凝土；裂缝；处理 　　Abstract: the concrete in the modern city construction has the important position, but with this kind of material used more widely, concrete structure crack also began increasingly attention by people. The cracks of the concrete structure will not only affect the structure of beautiful, also can affect the structure of durability and use fixed number of year. When the crack to a certain width, and then may endanger the safety of the building. Large number of research and practice have proved the concrete crack is inevitable, but science requirement is through certain method will control the degree of harmful in the appropriate range. 　　Keywords: concrete; Crack; processing 　　 　　 　　中图分类号：TU37文献标识码：A 文章编号： 　　1.混凝土裂缝的种类 　　混凝土是一种脆性材料，它的抗拉能力很低，在施工和使用过程中，当发生以下情况，如温度、湿度变化、地基不均匀沉降时，都很有可能产生裂缝。常见的混凝土裂缝有以下几种： 　　1.1 温度应力裂缝 　　此类裂缝产生的主要原因是由于在混凝土浇筑以后，内部的水泥水化热不容易散发，使得混凝土的内部温度升高，而混凝土表面与空气直接接触，散热较快，这样形成较大的内外温差，混凝土的内部产生压应力，表面产生拉应力。 　　1.2 塑性收缩裂缝 　　此类裂缝产生的主要原因是混凝土浇筑后，在处于塑性状态时表面水分蒸发速度太快造成的。 　　1.3 原材料质量引起的裂缝 　　混凝土的主要组成成分包括：水泥、砂、骨料、拌和水及外加剂。如果组成成分有质量不合格现象，就可能导致结构出现裂缝。 　　1.4 温度变形 　　混凝土的一个特性是热胀冷缩，因此在环境温度发生变化时，会产生温度变形，由此???生附加应力，当这种应力比混凝土的抗拉强度大时，就会产生裂缝。 　　1.5 湿度变形 　　混凝土在空气中结硬时，会出现干缩现象，体积逐渐减小。收缩裂缝较普遍，常见于现浇墙板式结构、现浇框架结构等，通常产生的原因是养护不良。 　　1.6 地基变形 　　在钢筋混凝土结构中，造成开裂主要原因是不均匀沉降。地基变形的情况会决定裂缝的大小、形状、方向，由于地基变形造成的应力相对较大，使得裂缝一般是贯穿性的。 　　2.混凝土裂缝成因 　　2.1 混凝土的收缩 　　收缩是混凝土的混凝土的收缩一个主要特性，对混凝土的性能有很大影响。由于收缩而产生的微观裂缝一旦发展，则有可能引起结构物的开裂、变形甚至破坏。 　　2.2 温度应力 　　温度应力。混凝土内的水泥在水化反应中散出大量热量，使混凝土升温，并与外部气温形成一定的温差，从而产生温度应力。其大小与温差有关，并直接影响到混凝土的开裂及裂缝宽度。 　　2.3 配筋不足 　　从实践中观察到，配筋间距大，配筋率小的混凝土结构开裂多，无筋混凝土比有筋混凝土开裂多。 　　2.4 混凝土材料及配合比 　　混凝土材料及配合比。配合比设计不当直接影响混凝土的抗拉强度，是造成混凝土开裂不可忽视的原因。配合比不当指水泥用量过大，水灰比大，含砂率不适当，骨料种类不佳，选用外加剂不当等，这几个因素是互相关联的。 　　2.5 养护条件 　　养护条件。养护是使混凝土正常硬化的重要手段。养护条件对裂缝的出现有着关键的影响。在标准养护条件下，混凝土硬化正常，不会开裂