浅谈桥梁工程质量通病原因及防治措施 　　摘要：随着近年来国家交通建设的大跨越大发展，各种桥梁的修建也越来越多，桥梁工程技术难度大，质量要求高，实行质量终身负责制，所以对桥梁的各种病害应引起充分的重视，在桥梁施工过程中对关键的工序进行质量控制，提前预防，避免日后出现病害，危害桥梁的使用寿命，降低桥梁的耐久性，本文将从以下几个方面来谈一下桥梁的质量通病原因及防治措施： 　　关键词：桥梁工程；病害；防治 　　Abstract: with the rapid development of national highway construction in recent years, a variety of bridgeconstruction is also increasing, bridge engineeringtechnology is difficult, high quality requirements, the implementation of quality lifelong responsibility system, so all kinds of diseases on the bridge should be paid much more attention to, in the process of bridge constructionon the key process quality control, advance prevention,to avoid future emerging diseases, endangering the life of the bridge, durability decreased bridge, this article will talk about the bridge from the following several aspects of thequality problems and prevention measures: 　　Keywords: bridge engineering; disease prevention; 　　中图分类号：U445文献标识码：A文章编号：2095-2104（2013） 　　 　　钢筋混凝土构造裂缝 　　 产生的原因： 　　1.水泥质量不好，如水泥安定性不合格等，浇筑后导致产生不规则的裂缝。 　　 2.骨料含泥量过大时，随着混凝土干燥、收缩，出现不规则的花纹状裂缝。 　　3、骨料为风化材料时，将形成以骨料为中心的锥形剥落。 　　4、混凝土搅拌和运输时间过长，导致整个结构出现细裂缝。 　　5、模板移动鼓出将使混凝土浇筑后不久产生与模板移动方向平行的裂缝。 　　6、基础与支架的强度、刚度、稳定性不够引起支架下沉、不均匀下沉，脱模过早导致混凝土浇筑后不久产生裂缝。 　　7、接头处置不当造成施工缝变成裂缝。 　　8、养护不到位不及时造成因混凝土表面收缩而造成裂缝。 　　9、大体积混凝土因受水化热及内外温差影响而产生的裂缝。 　　针对产生结构裂缝的原因，我们在施工中应采取针对性的预防措施： 　　选用优质的水泥和骨料 　　合理设计混凝土配合比，???善骨料级配、降低水灰比、掺加粉煤灰等掺和料、掺加缓凝剂、在工作条件能满足的情况下，尽可能采用较小水灰比及较低塌落度的混凝土。 　　避免混凝土搅拌很长时间后才使用。 　　加强模板的施工质量，避免出现模板移动、鼓出等问题。 　　基础与支架应有较好的强度、刚度和稳定性并应用预压措施，避免出现支架下沉，模板的不均匀沉降和脱模过早。 　　混凝土浇筑时要振捣充分，浇筑后要及时养护并加强养护工作。 　　大体积混凝土应优选矿渣水泥等低水化热水泥；采用遮阳凉棚等降温措施、布置冷却水管等措施，以降低混凝土水化热，同一结构物的不同位置温差应满足设计及规范要求。 　　桥面铺装病害的防治 　　（一）产生的原因： 　　梁体预拱度过大，桥面铺装设计厚度薄难以调整施工允许误差；施工质量控制不严，桥面铺装混凝土质量差；桥头跳车和伸缩缝破坏引起的连锁破坏；桥梁结构的大变形引起沥青混凝土铺装层的破坏，水害引起沥青混凝土铺装的破坏，铺装防水层破坏导致桥面铺装的破坏等。 　　（二） 防治措施 　　1龟裂的防治措施主要是在混凝土路面浇筑后及时的用潮湿的材料覆盖，认真的浇水养护，防止强风和暴晒，在配制混凝土时应严格控制水灰比和水泥用量，选择合适的粗骨料级配和砂率，在浇筑混凝土路面时，将基层和模板浇水湿透，避免吸收混凝土中的水分。 　　2加强对主梁的施工质量监控，避免出现预拱度过大。 　　3加强桥面铺装施工质量控制，严格控制钢筋网的安装。 　　4提高桥面防水混