不同伸长率钢筋在不同环境下氯离子侵蚀性能分析-analysis of chloride ion corrosion performance of steel bar with different elongation under different environments.docxVIP

AbstractCurrently, in the coastal region and in the region needs deicing salt melting in winter, the durability problem of reinforced concrete structures under chloride corrosion conditions, has received extensive attention of scholars. The corrosion of steel bars under chloride corrosion conditions exists as a main factor leading to structures failure. In reinforced concrete structures, as the stirrups provide much contribution to component of shear capacity, it is essential to study the degradation of stirrups mechanical properties. Preliminary research shows that the combination of plastic strain and corrosion causes additional damages. But study of this aspect is not completed. The specimens were not enough, and they were subjected to a plastic strain of just 4% which was such low. In view of above situation, this paper studies around the corrosion effect on different degree of the plastic strain of stirrups. In order to accelerate the experimental process and reasonably simulate actual engineering, this paper also explores the steel corrosion accelerating test method. The content includes:Analyze the effect of stirrups corrosion on the shear capacity of the reinforced concrete beams. Based on stirrups special formation, calculate stirrups different degree of the plastic strain in the bent corner.From some aspects, such as inducing rebar corrosion mechanism, corrosion products, surface morphology and degradation of stirrups mechanical properties, summarize the distinctions of the accelerating corrosion method. On this basis, put forward to a test method named ―High pressure-Dry-Wet cycle‖, which may better simulate actual corrosion of steel bars in the reinforced concrete structures.Experiment explored that the High pressure-Dry-Wet cycle test method is feasible. From some aspects, such as the surface features of the concrete specimens with corrosion steel bars and corrosion steel bars, surface morphology of cleaned corrosion steel bars and degradation of stirru