C40机制砂混凝土冻融循环强度研究.docVIP

C40机制砂混凝土冻融循环强度研究 　　摘要：目前，混凝土经受冻融循环后的力学特性方面的试验研究数量较为少见。水工、港工及海工混凝土结构由于冻融而损坏的现象较为严重，特别是有些混凝土结构虽按抗冻等级要求进行设计，仍发现有冻融损坏的现象，主要原因在于没有把结构的耐久性和结构的承载能力极限状态结合起来，没有充分考虑冻融后混凝土强度的降低。由于在冻融循环作用后，混凝土的力学性能将发生退化，因此研究冻融循环作用后混凝土的力学性能具有十分重要的工程意义。 　　关键词：C40机制砂混凝土；冻融循环强度；抗压强度试验；动弹性模量 　　Abstract: At present, the test and research of mechanical properties of concrete subjected to freeze-thaw cycles is relatively rare. The freeze-thaw damage in concrete structures of hydraulic, harbor and maritime work is more serious, even some concrete structures have been designed by antifreeze requirements, for which the major reasons are not the combination of structural durability and limit state of the carrying capacity, and not the consideration of the strength reducing after freeze thaw. As the mechanical properties of concrete structures will decline for freeze-thaw cycles, it is of great engineering significance to study the mechanical properties of concrete after freeze-thaw cycle. 　　Key words: C40 mechanism sand concrete; intensity of freeze-thaw cycles; test of compressive strength; dynamic elastic modulus 　　中图分类号：[TQ178]文献标识码：A 文章编号：2095-2104（2012） 　　主要仪器设备 　　试验中应用了多种试验设备，主要包括混凝土拌制及成型设备、力学性能测试设备、冻融循环试验设备、非破损检测设备等。 　　(1)混凝土拌制设备 　　本试验所用混凝土采用机械拌制，设备为无锡市华南实验仪器有限公司生产的SJD 60型单卧轴强制式混凝土搅拌机，额定容量为60L。 　　 　　图1-1SJD 60型单卧轴强制式混凝土搅拌机 　　(2)混凝土成型设备 　　本试验所用混凝土试模为100×100×400mm的混凝土冻融循环试验的标准试模，成型时采用上虞市土工仪器有限公司生产的振动台成型。 　　 　　图1-2振动台 　　(3)力学性能测试设备 　　本试验的抗压强度试验是采用液压压力试验机进行的。该加载设备最大加载为2000 KN。 　　 　　图1-3液压压力试验机 　　(4)冻融循环试验设备 　　本试验采用北京数智意隆仪器有限公司生产的KDR―3型混凝土快速冻融设备，由试验箱、机组、加热筒、管道泵、电控箱等组成。试验箱由箱体、保温层、保温门组成，箱体内采用不锈钢制造，箱体内设有冷冻液进出管，循环介质由下进上出，因此要求箱内液面高度必须浸没箱体上端的出液口。设备的设定温度上限为8℃±2，设定温度下限为-17℃±2，单个循环周期为2―4小时。 　　 　　图1-4KDR―3混凝土快速冻融试验机 　　(5)非破损检测设备 　　本试验的非破损检测包括试件质量检测及试件的动弹性模量检测。所用设备主要为台秤（称量10kg，精度1g），直尺（量程50cm，精度1mm），动弹性模量仪（测量频率范围：100Hz一10KHz；测量误差：小于3％：灵敏度：lmV；输出功率：0～15W；输出方式：数码管显示，示波管显示，打印机打印）。 　　 　　图1-5DT―10W动弹仪 　　原材料 　　本试验所用原材料为，水泥：42.5级普通硅酸盐水泥；机制砂：中砂，细度模数2.847；碎石：最大粒径20mm，连续级配；水：饮用水。 　　试验方法 　　本试