TC27钛合金的热变形行为及其组织演变规律-材料加工工程专业论文.docxVIP

PAGE PAGE IV up.  At the strain rate 0.001s-1 ~70s-1, rolling reduction 50%, 700 ℃, the alloy microstructure were similar with the original samples without deformation, the volume fraction of α phase in organization is more than those at other temperature. But in the high strain rate, such as the 70s-1, local flow and adiabatic shear can be observed in large deformation area. 850 ℃, the volume fraction of primary α phase compared to other temperature is least. deformation temperature from 900 ℃ to 1150 ℃, in the case of low strain rate, with increasing deformation temperature , the original β grain size increase further and the dynamic recrystallization were also more likely to happen in the interior of the grains, at last tiny recrystallization grain gradually replace the original rough grain. The suitable hot working parameters about forging state TC27 titanium alloy is: the deformation temperature from 700 ℃ to 1150 ℃, strain rate 0.001s-1, 0.01s-1and0.1s-1.while the instability area is easy happened at high strain rate (10s-1and70s-1) at various temperatures. Key words: As-forged TC27 titanium alloy, Hot deformation behavior, Constitutive relation, Microstructural evolution 南昌航 南昌航空大学硕士学位论文 目录 目录 摘要I Abstract II HYPERLINK \l _bookmark0 目录 IV HYPERLINK \l _bookmark1 第 1 章 绪论 1 HYPERLINK \l _bookmark2 1.1 钛合金的发展概况 1 HYPERLINK \l _bookmark3 1.2 钛合金分类 2 HYPERLINK \l _bookmark4 1.3 α+β 型钛合金的微观组织与性能 3 HYPERLINK \l _bookmark5 1.4 α+β 型钛合金的热处理及对其组织和性能的影响 4 HYPERLINK \l _bookmark6 1.5 本构关系 5 HYPERLINK \l _bookmark7 1.5.1 回归模型 6 HYPERLINK \l _bookmark8 1.5.2 内变量模型 7 HYPERLINK \l _bookmark9 1.6 本课题的研究内容与意义及目的 9 HYPERLINK \l _bookmark10 1.6.1 主要研究内容 9 HYPERLINK \l _bookmark11 1.6.2 研究意义 9 HYPERLINK \l _bookmark12 1.6.3 研究目的 10 HYPERLINK \l _bookmark13 第 2 章 试验材料试验方法 11 HYPERLINK \l _bookmark14 2.1 引言 11 HYPERLINK \l _bookmark15 2.2 试验材料 11 HYPERLINK \l _bookmark16 2.3 试验方法 11 HYPERLINK \l _bookmark17 2.3.1 相同加热温度不同保温时间下的试验 11