SS400含硼钢边裂机理研究-冶金工程专业论文.docxVIP

万方数据 万方数据 Abstract Because of SS400 boron-bearing steel having fine comprehensive properties and usability, which shows as high strength, good ductility and quick industrial production speed, it is widely used in production and living field. Boron element plays an important role in improving comprehensive performance of SS400 boron-bearing steel. However, in the actual production of SS400 boron-bearing steel, the slab edge cracking problem tends to exist with the addition of boron. In order to mitigate edge cracking of SS400 boron-bearing steel, this paper systematically studies on the mechanism of edge cracking of SS400 boron-bearing steel, and finds that the main reasons for the edge cracking of SS400 boron-bearing steel are the precipitation of BN particles and the remleting property of steel. The main contents of this paper are summarized as follows: The significance of studying on the mechanism of edge cracking of SS400 boron-bearing steel was clarified by introducing the research background, and the research status in related fields at home and abroad was also summarized. Based on analysis of edge cracking morphology of SS400 boron-bearing steel, the high temperature mechanical properties of steel was investigated through the Gleeble-1500 thermal simulator. In general, the high-temperature strength of SS400 boron-bearing steel decreases with the temperature increasing. Morever, there exist three brittle zones respectively named theⅠbrittle zone (1300 ℃ to the melting point), theⅡbrittle zone (1150℃ to 1250℃), and the Ⅲ brittle zone (700℃ to 950℃). The precipitation temperature of BN particles and the precipitation amount at various temperatures was calculated by thermodynamic method under the condition of SS400 boron-bearing steel chemical composition. The results show that the precipitation temperature of BN is much higher than AlN, and the nitrogen fixation of titanium in steel can reduce the amount of BN precipitation. Meanwhile, BN inclusions were detecte