Sr对Mg-9Li-3Al合金显微组织及高温力学性能研究材料加工工程专业论文.docxVIP

重庆大学硕士学位论文英文摘要 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV Moreover，the improved high-tempreture properties with Sr addition are analysed. Sr tends to separately form stable Al4Sr(1040℃) phase with Al in the alloys which leads to the reduction in amount of Mg17Al12、AlLi phases. The highly thermal stablility of Al4Sr phase could hinder dislocation climbing and slipping along the grain boundaries. The addition of Sr might cause the phase Al4Sr to be concentrated to the boundaries, which reduce the high-temperature properties of Mg-9Li-3Al alloy. On the contrary, minor content of Sr can improve the mechanical properties. Keywords：Mg-Li alloy, Sr, Extrusion Deformation, Microstructure, High-temperature mechanical properties 重庆大学硕士学位论文目录 重庆大学硕士学位论文 目 录 目 录 中文摘要 I 英文摘要II 1 绪 论 1 1.1 引言 1 1.2 镁合金发展概述 2 1.2.1 镁及镁合金基本特性 2 1.2.2 变形镁合金的研究前景 2 1.3 镁合金高温性能研究概述 4 1.3.1 镁合金塑形变形机理 4 1.3.2 镁合金高温强化机制 4 1.4 镁锂合金研究概况 6 1.4.1 主要镁锂合金系 6 1.4.2 镁锂合金研究现状及应用前景 8 1.5 本课题的研究内容、意义及创新点 9 1.5.1 课题研究内容 9 1.5.2 课题研究意义 10 1.5.3 课题的主要创新点 10 2 试样制备及研究方法 11 2.1 试验工艺流程 11 2.1.1 Mg-Li-Al-xSr 合金制备及微观组织研究路线 11 2.1.2 合金高温力学性能测试路线 11 2.2 合金的成分设计 11 2.3 试验制备工艺 12 2.3.1 原材料 12 2.3.2 镁基多元合金的制备 12 2.3.3 均匀化热处理 14 2.3.4 挤压变形 14 2.4 材料高温力学性能测试 15 2.4.1 测试设备 15 2.4.2 测试方法 15 2.5 材料的表征手段 16 2.5.1 合金实际成分的确定 16 2.5.2 金相观察 16 2.5.3 X 射线衍射分析 16 2.5.4 微区扫描电镜及能谱分析 16 2.5.5 高温拉伸断口扫描分析 16 2.6 本章小结 17 3 Sr 对 Mg-9Li-3Al 合金微观组织的影响研究 18 3.1 引言 18 3.2 实验合金的实际成分 18 3.3 铸态合金的微观组织分析 19 OM、SEM 形貌分析 19 EDS 能谱及 XRD 物相分析 22 3.3.3 Sr 对铸态合金细化机理探讨 26 3.4 实验合金均匀化热处理 26 3.4.1 均匀化处理工艺 26 3.4.2 均匀化热处理显微组织分析 27 3.4.3 XRD 物相分析 28 3.5 挤压态合金的显微组织 29 3.5.1 OM、SEM 形貌分析 29 3.5.2 挤压态合金 EDS 能谱分析 31 3.5.3 Sr 在挤压态合金中的存在形态分析 33 3.6 本章小结 33 4 Mg-9Li-3Al-xSr 合金高温力学性能研究 35 4.1 引言 35 4.2 铸态 Mg-9Li-3Al-xSr 合金的高温力学性能 35 4.2.1 Sr 对铸态合金高温力学性能的影响分析 35 4.2.2 铸态合金拉伸断口形貌分析 37 4.2.3 Sr 对合金高温力学性能影响分析 40 4.3 挤压态 Mg-9Li-3Al-xSr 合金的高温力学性能 40 4.3.1 Sr 对挤压态合金高温力学性能分析 40 4.3.2 挤压态合金拉伸断口形貌分析 42 4.3.3 不同状态合金高温力学性能比较 46 4.3.4 挤压态实验合金力学