碳纤维网格排列电磁屏蔽效率分析 　　本文研究了碳纤维平行和网格排列结构对 0.5 ～ 2.0 GHz频率内电磁波的屏蔽特性，实验结果表明材料的电磁屏蔽效能与碳纤维排布间距密切相关。此外，通过网格排列与不锈钢织物和平行排列屏蔽效能的对比，得出网格排列对电磁波衰减作用同网格状织物相似、与平行排列在所测频段内互补。 　　The electromagnetic wave (EMW) shielding effectiveness characteristics of the structure which carbon fiber arranged like grid in the frequency of 0.5 ~ 2.0 GHz were studied in this paper. The results showed that the EMW shielding effectiveness of this structure are affected greatly by the space between carbon filaments. In addition, the results also showed that the mechanism of EMW attenuation of grid arrangement is similar as grid shape fabric and complementary to parallel arrangement in the measured frequency. 　　 　　本文研究了通过碳纤维网格状排列来改变片状复合材料的屏蔽效率性，并与不锈钢纤维织物的屏蔽效能作对比，同时探讨了这类网格排列碳纤维材料的屏蔽效率特征，并论证了网格排列的作用。 　　1 试样制备及测试方法 　　1.1 实验材料 　　实验采用 200 tex/3 000 f的碳长丝束（由南通森友碳纤维有限公司提供）。实测单丝的平均直径 7.65 mm，密度为 1.44 g/cm3，电阻率为 0.044 Ω • m，碳长丝束的线电阻为 1.57 Ω/cm。试样的制备方法是将碳纤维长丝束伸直、平行地以一定间隔固定放置在发泡聚苯乙烯薄片（简称发泡PS片）上使之成网格状。发泡PS片的尺寸为 300 mm × 300 mm × 1.66 mm，柔软有弹性，类似于织物。碳长丝束的行间距为d，列间距为a，本试样的d＝a。具体试样编号与结构参数见表 1。由于发泡PS片对电磁辐射的吸收或屏蔽效能极小，可忽略。因此，取不锈钢纤维混纺制成的织物作为参照物，其组成和组织结构参数见表 2。 　　1.2 测试仪器及方法 　　1.2.1 测量系统 　　测量系统由 4 部分构成：①安立MG3642A型信号发生器，其作为电磁波信号源，频率范围为 125 kHz ～ 2.08 GHz，测量的动态范围大于 100 dB；②依据美国国家材料实验协会（ASTM）推荐的ASTM ?C ES ?C 7同轴传输线法进行改进的测量台；③安立MS2661C手持式频谱分析仪，分析频率范围为 9 kHz ～ 3 GHz，最小分辨带宽为 1 kHz，跟踪信号源最大输出功率超过 30 dBm；④与频谱分析仪相连的计算机。 　　测量系统的流程如图 1 所示。 　　1.2.2 测量方法与指标 　　本研究测定的指标为屏蔽效率（SE），ASTM D 4935平面材料电磁波屏蔽效能标准测试方法所定义。依据国家电子行业军用标准SJ 20524 ― 1995《材料屏蔽效能的测量方法》的规定进行。采用扫频方式进行测试，测量范围为 0.05 ～ 2 GHz，扫描间隔带宽为 0.01 GHz。测量方式如下： 　　其中，p1为测试台中不放置材料时频谱分析仪读数（dBm）；p2为测试台中放置纺织材料时频谱分析仪读数（dBm）；P1为测试台中不放置材料时的分析仪的接收功率；P2是测试台中放置纺织材料时的分析仪的接收功率。 　　2 实验结果与分析 　　2.1 平行排列间距对SE的影响 　　P1、P2、P3试样与一般电磁屏蔽服的不锈钢纤维混纺织物的测试结果对比如图 2 所示。从图 2 可发现，各个波峰的出现较集中，故下文将按低频段（0.2 ～ 0.8 GHz）、中频段（0.8 ～ 1.4 GHz）和高频段（1.4 ～ 2.0 GHz）分段进行分析。 　　在低频段，碳纤维试样的屏蔽曲线变化趋势相同，并随着间距的减小，即碳纤维质量的增加，吸收峰值依次增大，显然是因为碳纤维含量的增加，在入射电磁波的作用下，纤维表面产生更多的趋肤电流，从而通过欧姆损耗将电磁波能量转化为更多热能而消耗掉，还有平行排列的碳纤维PS发泡片构成了导电通道的作用，加剧了电