再生混凝土断裂能试验的研究 　　提要：本文依据国际混凝土协会（fib）2010模式规范建议，采用单轴拉伸试验，对再生混凝土的受拉断裂能进行了试验研究。根据实验结果，探讨了普通混凝土断裂能计算公式关系式对再生混凝土的适用性，结果表明普通混凝土断裂能计算公式不适用于再生混凝土。在试验数据回归分析的基础上，本文建议了再生混凝土断裂能计算公式，可供再生混凝土结构构件断裂分析时参考。 　　关键词：再生混凝土;断裂能;计算公式 　　Abstract: In this paper, on the basis of International Concrete Association (FIB ) 2010 model specification recommends, the uniaxial tensile test of recycled concrete, the tensile fracture energy are studied. According to the experimental results, and discuss the applicability of calculation formula of relation of recycled concrete can ordinary concrete fracture, the results suggest that in general the fracture energy of concrete calculation formula is not suitable for recycled concrete. Based on the regression analysis of experimental data, this paper suggests the recycled concrete fracture energy formula, the reference for the regeneration of concrete structure fracture. 　　Keywords: recycled concrete; fracture energy; calculation formula 　　 　　中图分类号：[TQ178]文献标识码A 文章编号 　　 　　 　　1 前言 　　近年来，随着环境保护意识和可持续发展观念的深入，关于再生混凝土技术的研究成为建筑材料和结构领域的一个热点问题。国内众多学者针对再生混凝土的力学、耐久和结构应用展开了大量的的研究工作，取得了许多重要成果，并且有了一些再生混凝土应用于实际结构和路面工程的实例，取得了良好的经济、环境和社会效益[1-2]。 　　混凝土的断裂能是其一个重要的断裂力学参数，该参数反映了混凝土抵抗断裂的能力。为了对再生混凝土结构进行断裂分析，需要提供这一参数的取值。在以往关于再生混凝土断裂能的试验研究中[3-4]，研究者的试验一般是参照RILEM 1985 TC50-FMC[5]建议，采用三点弯曲梁方法作为试件，所用梁为缺口梁。这种试验方法的主要缺点是：梁的自重会对试验数据产生一定的影响；另外，由于梁转动效应的影响，试验所采用的骨料影响很大。因此，在国际混凝土学会最新规范Model Code (MC) 2010[6]中，推荐采用单轴直接拉伸试验来测定混凝土的断裂能。本文采用这一建议，对再生混凝土的断裂能进行了初步的试验研究，建议了再生混凝土断裂能的计算公式。本文的研究结果可以应用于再生混凝土结构的断裂分析。 　　2 试验研究 　　2.1 原材料 　　试验中所用的水泥为普通硅酸盐水泥，分为两种，即32.5R和42.5R，其中32.5R水泥用于配制强度等级为C20-C30再生混凝土，42.5R水泥用于配制C35再生混凝土。砂为普通黄砂，细度模数为2.75。再生粗骨料由某拆除废弃混凝土建筑物构件经破碎加工而成，连续级配，粒径范围为5-31.5 mm，其堆积和表观密度分别为 1285 和 2502 kg/m3，吸水率为6.28%， 压碎指标为10.2 %。 拌和水为普通自来水。 　　2.2 混凝土配合比 　　由于再生粗骨料品质较天然碎石或卵石差，一般建议采用再生骨料配制C40以下的混凝土。本文共配制了C20、C25、C30和C35共4种强度等级再生混凝土。由于再生粗骨料吸水率较高，在配制混凝土之前对其进行了润湿，达到饱和面干状态。各强度等级再生混凝土的配合比在参考文献普通混凝土常用配合比的基础上通过调整水泥用量经反复试配最终确定，具体的材料配合比如表1所示。 　　表2 混凝土的配合比 　　 　　 　　2.3 试件的准备及试验方法 　　混凝土采用人