高温淬火对3Cr2W8V钢组织性能的影响.PDFVIP

高温淬火对 3Cr2W8 V 钢组织性能的影响 ( ) 佛山市火花塞厂 广东佛山 528031 　廖嘉琪 　江韶光 ( ) 【摘要】　利用 X 射线衍射和透射电子显微镜 TEM 研究了 3Cr2W8V 钢高温淬火后回火对显微组织和力学性能的影响 ,着重 讨论了回火转变与冲击韧度的关系。试验表明高温回火脆性与残留奥氏体分解和沿晶界碳化物析出有关。 关键词 :3Cr2W8V 模具钢 　高温淬火 　中温回火 　深冷处理 Effect of High Temperature Quenching on Structure and Properties of 3Cr2W8 V Steel ( park Plug Factory ,Foshan 528031) Liao Jiaqi ,Jiang Shaoguang Foshan S 【Abstract 】　The effect of high temperature quenching followed by tempering on microscopic structures and mechanical properties of 3Cr2W8V steel has been studied by using XRay Diffraction and Transmission Electron Microscope ( TEM) . The relationship of tem pering transformation and punching toughness of the steel has been emphatically discussed. The experimental results indicate that the high temperature tempering embrittleness is related to the decomposition of retained austenite and the precipitation of carbide along the grain boundaries. Key words :3Cr2W8V die steel ,high temperature quenching ,medium temperature tempering ,deep cool treatment 1 　前言 盐浴中奥氏体化 10min 后油冷。为了体现残留奥氏体的影 ( 响 ,部分试样进行了深冷处理 ,即将油冷试样立即放入液氮内 3Cr2W8V 钢是一种用途广泛的钨系热模具钢。经 1050 ( ) ～1100) ℃奥氏体化后淬火的常规热处理组织中 ,约有 5 %～ 深冷 5min 。回火在空气炉中进行 ,经 200 ～600 ℃不同温度 7 %的未溶碳化物 ,因此模具的热稳定性较差 , 易于发生软化 回火两次 ,每次 2h 。 造成早期磨损和局部软塌。近年来 , 国内外研究者提出高温 2 3 　性能测试 淬火 + 中温回火工艺[ 1 ,2