低频导波技术在炉管检测中的应用.PDF

检测技术 第 3 1 卷 第 11 期 低 频 导 波 技 术 在 炉 管 检 测 中 的 应 用 韩利哲 湛小琳 丁 敏 （中国特种设备检测研究院 北京 100029) 摘 要：炉管的两种主要失效形式是开裂和腐蚀减薄。本文通过人工缺陷样管检测实验和现场实验研究 探索磁致伸缩超声导波技术在炉管检测中的可行性。结果表明：炉管结焦对导波传播影响很小，应用磁致伸 缩超声导波技术检测时，无须对炉管内表面进行处理；磁致伸缩超声导波技术可以准确检出炉管开裂和腐蚀 减薄类缺陷，并可进行轴向定位。磁致伸缩超声导波技术应用可使炉管检测更快速和有效。 关键词：超声导波 炉管 无损检测 The Application of Low Frequency Guided Wave in Furnace Tubes Detection Han Lizhe Zhan Xiaolin Ding Min (China Special Equipment Inspection and Research Institute Beijing 100029) Abstract Cracking and etching thinning are two main failure modes of furnace tubes. This paper focus on the feasibility of low frequency guided wave in furnace tubes detection. Experiments have been conducted on sample tubes with different artificial defects and field furnace tube. The results indicate that coking has little influence on guide wave transmission, so the furnace tubes don’t need surface treatment before detection. Besides, the cracking and etching thinning defects could be identified and the axial position of the defects could be given. The furnace tube defection will become more accurate and efficient with the application of magnetostriction ultrasonic guide wave technology. Keywords Ultrasonic Guided Wave Furnace tube Nondestructive testing 中图分类号：X924.2 文献标识码：Ｂ 文章编号：1673－257X(2015)11-0025-07 DOI: 10.3969/j.issn.1673-257X.2015.11.007 1 炉管检测现状 输管线的检测技术，已被广泛应用。本文尝试将此技 术引入到炉管检测中，通过人工缺陷样管检测实验和 炉管是裂解炉和转化炉的关键部件，通常采用离心 现场检测研究低频导波技术在炉管检测中的可行性和 铸造成型，并且成型后表面形成一层杨梅粒子涂层 [1] 。 有效性。 炉管常用材料为高温铬镍合金，在使用过程中存在蠕 变、热疲劳、弯曲、高温氧化以及渗碳等多种损伤机理， 2 实验研究 在诸多损伤机理作用下，炉管主要失效形式表现为开 裂和腐蚀减薄。由于制造工艺和结构特点，目前用于