新型无机快速堵漏砂浆应用研究-龙湖科技.PDF

型无机快速堵漏砂浆应用研究 胡明 罗慧 罗庚望 广东龙湖科技股份有限公司北京技术中心 要：目前在市场上无机快速堵漏产品，使用硫铝酸盐水泥为胶凝材料较为普遍，但由于硫铝酸盐水泥收缩大、 易粉化后期强度倒缩，从而在应用中存在抗渗性差等问题。本研究以普通硅酸盐水泥为胶凝材料复配使用新型快 硬材料研发无机快速堵漏砂浆，研究结果表明：使用新型快硬材料堵漏砂浆1 小时抗压强度在4.5-30MPa 可控， 同时能够大幅度减小砂浆收缩率提高抗渗性能，另外在低温环境中具有良好的施工性能。 关键词：无机快速堵漏砂浆、新型快硬材料、干燥收缩、抗渗强度 HU Ming, LUO Hui，LUO Gengwang (Beijing Technical Center Guangdong Longhu Sci. Tech.Co.Ltd, 100076, Beijing, China) Abstract: At present, the most of cementing material is SAC in the Inorganic leakage-preventing mortar, because of SAC has same bad characteristics, such as high shrinkage and compressive strength retracted etc..In the practical application,these bad characteristics are prone to destroy the anti-penetrating performance of Inorganic leakage-preventing mortar. In this study,using ordinary portland cement as cementitious materia by compounding ACA to develop a new Inorganic leakage-preventing mortar.This research show that using ACA can obtain high strength and low shrinkage Inorganic leakage-preventing mortar.It also has a good construction performance in low or high temperature environment. Keywords: Inorganic leakage-preventing mortar，New repid-hardening material，Drying-shrinkage ， Anti-permeability strength 1 前言 随着我国国民经济持续快速发展，带动了建筑产业的高速增长，无机快速堵漏砂浆无论是在新楼房建 造，还是在其他水泥混凝土结构维护，都有广泛的应用。在市面是常用的无机堵漏砂浆主要有两类：普通 [1] [2] 硅酸盐水泥和硫铝酸盐水泥复配 ；纯硫铝酸盐水泥与速凝剂复配 。但是硫铝硅酸盐水泥与普通硅酸盐 水泥化学的差异，导致凝结时间存在很大的波动，同时纯硫铝酸盐水泥与速凝剂复配的堵漏剂易吸水受潮 变质，施工过程中耐低、高温性差，施工硬化后强度倒缩等问题，严重影响着堵漏剂的使用。本文以普通 硅酸盐水泥为胶凝材料，添加新型快硬材料等添加剂配 无机快速堵漏砂浆，并研究新型快硬材料对快速 堵漏砂浆性能的影响。 2 原材料和实验方法 2.1 原材料 水泥：冀东42.5 级普通硅酸盐水泥； 水洗河砂：SiO 含量＞92%，粒径分布为 0.1-0.3mm； 2 石英粉：0.05-0.1mm； 可再分散乳胶粉：VINNAPAS 8034H； 纤维素醚：Tylose MH6