第二试浇块试验总结.doc

PAGE PAGE 1 Test Report for the Second 2m Cube Trial 1．The Purpose of the Second trail Pour of Bigger Samples For the proposed new mix ratio, monitor the temperature cha Samples nge, internal strain, surface appearance and crack development, verify the efficiency of the new temperature control measures , curing methods and basic performances of concrete; Then compare the results of the second trial block with the first one to obtain better methods for concrete casting. 2．Comparison for the 2 trial blocks Table 1 comparison for the 2 trial blocks The 1st trial block The 2nd trial block Mix ratio 配合比 Slump 塌落度 Leaving plant: 150mm Slump Leaving plant: 120mm Before placing: 90mm Before placing: 80mm Temperature before placing 27 Temperature before placing 29 Setting time 凝固时间 Initial setting: 6hrs 初凝 Setting time Initial setting: 18 hrs Final setting time: 7.5 hrs Final setting time: 20hrs： Mechanical properties of the concrete 砼机戒性能 Compressive strength for 3 days: 37MPa Compressive strength for 3 days: 31.5MPa Tensile strength for 3 days: 3.18N/mm2 Tensile strength for 3 days: 2.53N/mm2 Elastic module for 3 days: 23250N/mm2 Elastic module for 3 days: 12200N/mm2 Results of temperature and strain Temperature Maximum temperature: 71 Temperature Maximum temperature: 72 Maximum concrete temperature difference: 41 Maximum concrete temperature difference: 25 Strain Central point for 3 days: 96.82 Strain Central point for 3 days : 126.54 Curing Covered with thin sacks, and polythene. Removing the polythene when pouring water. Covered with 3 layers of geotextile, and covered with polythene for all day. Did not remove the polythene when pouring water with dripper pipe feeding water. The temperature of the curing water was controlled at 35±5℃ Plum No P Place 3 layers of plum, which occupy 6% of the total volume of the concrete Admixture CF100: 5.3 L/m3 (1.8% of the cement by weight) CP305:1.1 L/m3 (0.36% of the cement by weight) SP435: 5.4 L/m3 RP264: 0.77 Kg/m3 3．The Par