耐火填料对铸造涂料质量的影响 朱剑甫 (郑州翔宇铸造材料有限公司，河南郑州 450016) 摘要：铸造涂料影响铸件的内在及表面质量，尤其是消失模涂料是控制并保证消失模铸造质量的关键因素之一。众所周知，铸造涂料是由载体、耐火填料、悬浮剂、粘结剂和辅助添加剂五种基本组分组成，其中耐火填料为主要组分，它决定着涂料的耐火度、化学稳定性、绝热性，对涂料的透气性、烧结剥离性也有重要影响。因此可以说耐火填料的质量是铸造涂料质量的关键因素。 本文就翔宇公司多年来生产的各种铸造涂料及耐火填料作些总结及探讨，供铸造厂家和同行们参考。 关键词：消失模铸造，耐火填料，涂料质量 Influence of Refractory Fillings on the Quality of Coating on EPC ZHU Jianpu (Zhengzhou Xiangyu foundery materials Co.,Ltd.,Zhengzhou 450016,Henan) Abstract: The foundry coating influences the internal and surface quality of castings. And it is one of key factors to control and ensure the casting quality on EPC. As is now well known,foundry coating is consist of 5 kinds of basic components such as carrier material,refractory fillings, defocculaing aent, binding agent and accessorial addition agent. In which the refractory fillings is its main components that it decides the refractoriness,chemical stability, diathermancy of the coating ,simultaneously it influences also the gas permeability,sinter delaminating property of the coating.Therefore it is observed that the quality of refractory fillings is a key factor to affect foundry coating quality. In this paper the summary and discussion are made on all kinds of foundry coatings and its refractory fillings by Xiangyu foundry materials Co.,Ltd.for a reference to foundries and fellows Key words: EPC, refractory fillings,coating qualities 在消失模铸造中，如何选用涂料的耐火填料，主要考虑填料的如下性质： （1）耐火度； （2）密度； （3）热膨胀系数； （4）粒型与粒度分布； （5）与金属液的化学反应性； （6）发气量； （7）与涂料中其它成份的互融性； （8）对操作工人健康与环境是否影响。 1、铝矾土粉 铝矾土以其耐火度高、化学稳定性好，膨胀系数小且来源丰富、价格低等特点，近年来在普通铸造钢涂料及铸铁涂料中广泛应用。 1．1化学成分 铝矾土中的Al2O3?含量、烧结温度及Ti02、FeO3 等杂质含量对涂料影响较大，因此选用Al2O3?含量高的矿石经1450℃-1500℃锻烧后，精选熟料研磨，制成细粉后，酸洗处理仍是关键一步，不经酸洗处理的铝矾土除Ti0 1.2粒度 铝矾土的粒度及粒度分布是影响涂层致密度和透气性的重要因素，特别是消失模涂料，泡沫塑料模样在烧结过程中的热解产物通过涂层能否顺利排出，消失模涂料的透气性是区别于其它砂型铸造涂料的一大特点。翔宇公司根据不同需要，将铝矾土的粒度级配成两种不同规格分别使用于砂型铸造涂料和消失模涂料中。 砂型铸造涂料所用铝矾土粉的粒度分布为： -270目至320目，集中率为96 % +270目 不大于1% 消失模涂料所用铝矾土的粒度分布为： -270目至-320目 78% -200目至-270目 15% -100目至-200目