工业化冷床熔炼技术的引进与应用-中国有色金属学报.PDF

20 1 2010 10 Vol.20 Special 1 The Chinese Journal of Nonferrous Metals Oct. 2010 1004-0609(2010)S1-s0877-04 ( 200940) TF 804.3 A Introduction and application of industrial cooling hearth melting technology QIN Gui-hong, WANG Wan-bo, JI Bo, WU Ying-yan (Baoshan Iron Steel Co., Ltd., Shanghai 200940, China) Abstract: The cooling hearth melting technology is advanced melting technology. The high quality titanium alloy ingot can be produced by single melting. The development survey of cooling hearth melting was introduced. The character and working principle were contrasted. The advantage on manipulation control and removal of inclusion was pointed out. At the same time, plasma cooling hearth melting (PACHM) and electric beam cooling hearth melting (EBCHM) were introduced in detail. Keywords: cooling hearth melting; titanium alloy; melting technology 90%3 VAR 0.8 mm WC 3 VAR 4 F-22 41%F119 39%[1] 20 (Vacuum arc remelting, VAR) —— 2 (Cold hearth melting, CHM) 2 VAR 3 VAR [2] 1 3 VAR RUDINGER (Plasam 0.6 mm WC 2 VAR arc, PA)(Electron beam, EB) 021E-mail: qinguihong@ s878 2010 10 1 Fig.1 Working schematic diagram of CHM 1963 6) 2 (EBCHM+VAR) 1988