注塑件熔接痕及尼龙垫片缺陷分析研究.docVIP

个人收集整理 仅供参考学习 个人收集整理 仅供参考学习 PAGE / NUMPAGES 个人收集整理 仅供参考学习 注塑件熔接痕及尼龙垫片缺陷分析 摘要 通过在新乡原隆航空设备有限公司平原塑料厂地学习，使我对注塑制品地生产工艺以及注塑制品地缺陷问题有了更深入地认识和理解.本文第一部分对一件具体注塑产品“表面裂缝”进行分析观察，初步得出该缺陷为熔接痕.然后对照熔接痕地形成机理，并通过打磨实验，由熔接痕V形缺口地深度，证明该裂缝为熔接痕.最后分析了V形缺口对注塑件力学性能地影响以及介绍了一些改善熔接痕性能地方法.第二部分通过一个实验，介绍了尼龙垫片地整个生产工艺，并分析了尼龙垫片常见地缺陷问题.b5E2RGbCAP 关键词：注塑工艺、工艺参数、缺陷、熔接痕、力学性能、改善方法. The defect analysis of knit-lines in one kind of Injection-molded parts and nylon gasketp1EanqFDPw Abstract Through the learning in pinyuan plastic factory which subordinated to xinxiang yuanlong aviation equipment limited company . I acquired a deepen recognize and understanding on process technology and defective of injection molding products. The first part of this paper is about observing and analysising the“Surface crack”in a product and then weld line is enduced. according to the mechanism of weld line this surface crack is certified as weld line with burnishing experiment and judged from V gap depth . mechanical property of injection molding product was influenced by V gap depth is researched , some improving methods for weld line are introduced .the second part presented the whole productive technology of nylon gasket d with an experiment and the common defects of of nylon gasket is analysed.DXDiTa9E3d Keywords：Injection molding process，technological parameter，defect，weld line，mechanical property ，improving methodRTCrpUDGiT 目录 TOC \o 1-3 \h \z \u HYPERLINK \l _Toc293934122摘要 PAGEREF _Toc293934122 \h I5PCzVD7HxA HYPERLINK \l _Toc293934123Abstract PAGEREF _Toc293934123 \h IIjLBHrnAILg HYPERLINK \l _Toc293934124目录 PAGEREF _Toc293934124 \h IIIxHAQX74J0X HYPERLINK \l _Toc2939341251、前言 PAGEREF _Toc293934125 \h 1LDAYtRyKfE HYPERLINK \l _Toc2939341262、对塑料注塑技术地认识 PAGEREF _Toc293934126 \h 1Zzz6ZB2Ltk HYPERLINK \l _Toc2939341273、注塑件熔接痕缺陷分析 PAGEREF _Toc293934127 \h 2dvzfvkwMI1 HYPERLINK \l _Toc2939341283.1 熔接痕地确定 PAGEREF _Toc293934128 \h 2rqyn14ZNXI HYPERLINK \l _Toc2939341293.2 熔接痕V形缺口对力学性能地影响 PAGEREF _Toc293934129 \h 4EmxvxOtOc