热连轧Ti-6Al-4V合金的蠕变行为及影响因素-中国有色金属学报.PDF

20 2 2010 2 Vol.20 No.2 The Chinese Journal of Nonferrous Metals Feb. 2010 1004-0609(2010)02-0250-07 Ti-6Al-4V 1 1 2 1 1 2 (1. 110178; 2. 110004) Ti-6Al-4V β α 1 000 940 1 000 420 575 MPa 249.8 kJ/mol HCP α940 〈a+c〉α1 000 (1/2)〈111〉BCC β 1 000 V β Ti-6Al-4V 146.2 A Creep behaviors and effect factors of hot continuous rolled Ti-6Al-4V alloy 1 1 2 1 1 2 TIAN Su-gui , BAO Xian-yu , CHEN Li-qing , LIU Yang , ZHAO Zhong-gang , LIU Xiang-hua (1. School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110178, China; 2. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, China) Abstract: By heat treatment, measurement of creep properties and contract analysis of dislocations configuration, the creep behaviors and the effect factors of hot continuous rolled (HCR) Ti-6Al-4V alloy were investigated. The results show that, after the alloy solution treated at temperatures lower than β phase transformation point, the microstructures of the alloy consist of the supersaturation equiaxial α phase and network basket structure. The quantities of the network basket structure increase as the solution temperature increases, and the full network basket