毕业论文-纤维素共价固定功能化酞菁.docVIP

本科毕业论文 （20 届） 纤维素共价固定功能化酞菁 专业：高分子材料与工程 摘 要：本实验探索一种将酞菁功能分子共价固定到纤维素上的新方法。首先制备得到乙酸纤维素薄膜，并使其水解转化成纤维素。再以高碘酸钠为氧化剂将已水解的纤维素薄膜氧化。最后将金属酞菁溶于DMF中加热负载到纤维素纤维上，制备得到一种金属酞菁负载纤维素纤维薄膜。并探讨了反应条件对酞菁固定量的影响。 关键词：金属酞菁；合成；纤维素纤维；负载 Covalent immobilization of cellulose functional phthalocyanine Abstract: In this paper, a new method for covalently immobilization of phthalocyanine onto cellulose film was discussed. First cellulose acetate film was prepared and then hydrolyzed to cellulose film. The obtained cellulose film was further oxidized to form reaction groups on the surface. Phthalocyanine was then immobilized onto the film. The influence of reaction time and reaction temperature on the immobilized amount was also discussed. Key words: Metal phthalocyanine;Synthesis;Cellulose fiber;Immobilization 目 录 TOC \o 1-3 \h \u HYPERLINK \l _Toc8565 1.引言 PAGEREF _Toc8565 1 HYPERLINK \l _Toc20976 2.实验部分 PAGEREF _Toc20976 3 HYPERLINK \l _Toc2476 2.1 实验原料 PAGEREF _Toc2476 3 HYPERLINK \l _Toc25498 2.2 实验仪器 PAGEREF _Toc25498 3 HYPERLINK \l _Toc31836 2.3 固定方法的选择 PAGEREF _Toc31836 3 HYPERLINK \l _Toc166 2.4载体的选择 PAGEREF _Toc166 4 HYPERLINK \l _Toc392 2.5合成四氨基金属酞菁的原理及其过程 PAGEREF _Toc392 4 HYPERLINK \l _Toc10574 2.6纤维素薄膜的制备与固定过程 PAGEREF _Toc10574 5 HYPERLINK \l _Toc30632 2.7薄膜的性能的测定 PAGEREF _Toc30632 6 HYPERLINK \l _Toc11466 3. 结果与讨论 PAGEREF _Toc11466 6 HYPERLINK \l _Toc6468 3.1紫外光谱的分析 PAGEREF _Toc6468 6 HYPERLINK \l _Toc10985 3.2红外光谱的分析 PAGEREF _Toc10985 7 HYPERLINK \l _Toc16558 3.3示差量热扫描仪DSC PAGEREF _Toc16558 7 HYPERLINK \l _Toc28524 3.4反应时间对酞菁纤维素固定的影响 PAGEREF _Toc28524 8 HYPERLINK \l _Toc25211 3.5反应温度对酞菁纤维素固定的影响 PAGEREF _Toc25211 9 HYPERLINK \l _Toc23845 4. 结论 PAGEREF _Toc23845 9 HYPERLINK \l _Toc15509 参考文献 PAGEREF _Toc15509 10 HYPERLINK \l _Toc3883 致谢 PAGEREF _Toc3883 12 PAGE 1 1.引言 随着工业的迅速发展和城市人口的集中,在生产和生活中排放的各种污染物越来越多,严重影响着人们的正常生活。传统方法大多是采用物理吸附使其除去或喷洒空气清新剂掩盖其臭味,但存在饱和吸附、吸附剂再生困难或不能将毒害真正消除等问题。酞菁作为一种着色剂已广泛应用于涂料、印刷和纺织行业,近年来,金属酞菁因其结构特点在作为催化剂应用上也被广泛的研究,能够催化包括加