6061铝合金搅拌摩擦焊工艺.docxVIP

铝合金搅拌摩擦焊工艺6061陈舟，周友龙，田博，张 腾，刘拥军(西南交通大学 材料学院，四川 成都 铝合金搅拌摩擦焊工艺 6061 陈 舟，周友龙，田 博，张 腾，刘拥军 (西南交通大学 材料学院，四川 成都 610031) Research on FSW of 6061 aluminum alloy CHEN Zhou，ZHOU You-long，TIAN Bo，ZHANG Teng，LIU Yong-jun (Material Processing Engineering，Southwest Jiaotong University，Chengdu 610031，China) Abstract：6061 aluminum alloy plates of thickness 6mm are jointed by friction stir welding(FSW) in different parameters．The influence of the main parameters with joint shaping and the mechanical properties of joints is studied．The microstructure of the joint is observed．The Mechanics inhomogeneity is researched by hardness testing．The results show that high quality welds can be got at 0．3 mm pressed amount．Some forming defects would be caused under the station of the oversize or undersize of the pressed amount．The tensile strength is 196 MPa which reaches the 79．7％ strength of the base material at travel speed of 200 mm／min and rotation speed of 1 100 r／min． The distribution of Hardness of the FSW joints shows like ″W″－type，there is a clear softening zone．The lowest hardness can be found in the forward side of the heat-affected zone． Key words：friction stir welding；6061 aluminum alloy；pressed amount；microstructure 前言 6061 铝合金属 Al－Mg－Si 系合金，中等强度， 具有良好的塑性和耐蚀性，无应力腐蚀开裂倾向， 焊接性能优良，耐蚀性和冷加工性好，作为结构材 料被广泛用于建筑、交通、能源等领域，尤其在高速 铁路中作为动车轻量化材料之一，其应用更加受到 关注。 搅拌摩擦焊(FSW)是固相连接，热输入低，与传 统熔化焊相比，具有焊接缺陷少、力学性能优异、焊 接变形和残余应力小等优点，是一种优质、高效、耗 能低的新型焊接方法[1－3]。 试验方法 焊接试验使用材料为 6 mm 厚的 6061－T6 铝 合金轧制板材，化学成分如表 1 所示，常温拉伸强 度 246 MPa。 0 1 表 1 6061 铝合金化学成分 ％ 搅拌头采用圆锥带螺纹搅拌针加内凹锥面轴 肩设计，轴肩直径 23．1 mm，螺旋型搅拌针直径为 5．7 mm，长 5．7 mm。试验时，先用砂纸和钢丝刷清除 待焊部位的杂质和氧化膜，并用丙酮清洗，然后用 专用夹具将试验板装夹在工作台上，并严格保证待 焊面紧密接触。焊接参数为：搅拌头转速 1 100 r／min， 焊接速度 150～320 mm／min。焊接完成后，选取焊缝 成形良好的试板加工拉伸试样、硬度试样和金相试 Electric Welding Machine · 95 · 收稿日期：2011－10－13 基金项目：中央高校科技创新基金资助项目(A0920501102－51) 作者简介：陈 舟(1988—)，男，四川广安人，在读硕士，主要 从事铝合金搅拌摩擦焊接工艺的研究。 w(Si) w(Fe) w(Cu) w(Mn) w(Mg) w(Cr) w(Zn) w(Ti) w(Al) 0．53 0．38 0．33 0．04