毕业论文：《吸附法去除废水中的氨氮》.doc

l l l 吸附法去除废水中的氨氮 摘 要 本文通过静态吸附试验研究了吸附法去除废水中的氨氮，筛选出了适合的吸附剂，及其最佳吸附条件和最佳改性条件，以及计算再生损耗量。结果表明，沸石对氨氮的吸附量明显大于活性碳和腐殖酸；在常温下最佳吸附条件是废水pH值为10~12；最佳改性条件是温度为60℃，2mol/L NaOH浸泡改性8h，用无氨水反复冲洗，105℃烘干2h；选择10%NaCl溶液，与浓度为0.4mol/L的NaOH溶液等体积混合为再生剂，浸泡4h再生，105℃烘干备用，经测定，再生后的沸石可完全恢复其吸附能力，且其再生损耗为0.437%，工业上经济可行。 关键字：氨氮 吸附 沸石 改性 再生 Abstract The removal of wastewater containing ammonia by adsorption under static condition is researched in the paper. A suitable adsorbent, its best adsorption and capacity altering conditions are scalped, and test the regeneration ability of the adsorption. The result indicates, the capacity of zeolite for removal ammonia is much better than active C or humus acid; The best condition of adsorption is under room temperature and the pH is between 10 and 12 of the wastewater; The best condition of capacity altering is under 10℃, dipped in 2mol/L NaOH for 8h, washed by no ammonia water, hot under 105℃ 2h; 10% NaCl and 0.4mol/L NaOH confuse by the same volume to be the regeneration liquid, dipped for 4h to regenerate, hot in 105℃ for spare, after the test, the regenerated zeolite can completely renew its capacity of adsorption for ammonia, and its wastage after regeneration is 0.437% , it is economical to industry. Key words: ammonia adsorption zeolite capability altering regeneration 目 录 TOC \h \z \t 1,1,2,2,3,3 摘 要 h I Abstract h II 第一章 绪 论 h 1 1.1氨氮废水来源 h 1 1.2氨氮废水的危害 h 1 1.3氨氮废水的处理方法 h 2 1.3.1生物法 h 2 1.3.2物理化学法 h 3 1.3.3组合方法 h 5 1.3.4吸附法的概述 h 5 1.4国内外氨氮废水处理现状 h 8 1.4.1国外研究现状 h 8 1.4.2国内研究现状 h 8 1.5本试验研究的目的和意义 h 8 第二章 吸附法去除废水中氨氮的试验研究 h 9 2.1试验所需药剂及仪器 h 9 2.2氨氮测定标准曲线的绘制 h 9 2.3吸附剂的初步选择 h 10 2.3.1不同吸附剂吸附量的比较 h 10 2.3.2不同粒度沸石的吸附量 h 11 2.4沸石的最佳吸附条件 h 12 2.4.1pH值的影响 h 12 2.4.2温度的影响 h 12 2.5改性方法研究 h 13 2.5.1不同改性方法的对比 h 14 2.5.2不同浓度NaOH改性的影响 h 15 2.5.3改性温度的影响 h 15 2.5.4改性时间的影响 h 16 2.6沸石再生试验 h 17 2.6.1再生药剂的选择与再生效果 h 17 2.6.2沸石再生损耗 h 18 第三章 试验结论、评价与建议 h 19 3.1