新型混凝土耐磨剂关键技术研究报告 作者：柯旭，崔凯，张晓玲 （贵州师范大学，材料与建筑工程学院，贵阳，550025） 摘要：首先从宏观到微观，在不同尺度上研究混凝土在挟沙水流作用下的冲磨破坏机理。 然后利用正交试验研究膨胀剂、MP 和过0.045mm 筛的粉煤灰的掺量对水泥基复合材料强度 的影响；同时借助扫描电子显微镜（SEM）等对胶凝材料微观结构进行分析。试验结果表明： 膨胀剂掺量对水泥基材料的强度影响较大，其次是筛过后的粉煤灰，再次是MP；另外通过 试验得出了配制强度达到50MPa 的水泥基复合材料的具体配合比，即膨胀剂掺量6%、MP 掺 量5%、粉煤灰（筛）掺量8%，而且该新型耐磨剂的抗冲耐磨性能较普通混凝土提高50%。 关键词：冲磨破坏机理；正交试验；配合比；微观结构 Abstract: First, from the macroscopic to the microscopic, on different scales to study the concrete under the action of sediment-laden flow erosion mechanism. The effects of the dosage of expansion agent, MP and 0.045mm sieve on the strength of cement - based composites were studied by orthogonal test. The microstructure of cementitious materials was also analyzed by scanning electron microscopy (SEM). The results show that the swelling agent has a great influence on the strength of the cement-based materials, followed by the fly ash after sieving and MP again. In addition, the concrete compaction ratio of the cement-based composites with the preparation strength of 50MPa , The swelling agent content of 6%, MP content of 5%, fly ash (sieve) content of 8%, and the new wear-resistant abrasion resistance of ordinary concrete increased by 50%. Key words: crushing failure mechanism; orthogonal test; mix ratio; microstructure 1 引言 1.1 研究背景 我国河流众多，而且很多都是从高原地区流向平原地区。以黄河为例，黄河 中上游大多都是高原山地，中段流经黄土高原，所以黄河每年都会有16 亿吨左 [1] 右泥沙产生，成为了全球少见的多砂河流 。高速含砂和推移质水流对水工混凝 [1-3] 土的破坏长期以来备关注，也是专家学者急需解决的问题之一 。据调查，我 国的大坝泄水建筑物有70%左右被含砂水流冲磨破坏，有的还危及其他建筑物。 [4] 其中丰满、三门峡、刘家峡、等工程虽对病害进行了修复但还是反复被破坏 。 20 世纪80 年代中期以来，各种抗冲磨混凝土在我国逐渐得到应用，我国许 多水利科研单位与材料生产厂家先后开展了水工泄水建筑物抗冲磨材料及工艺