第九章 海洋环境腐蚀特征与电化学研究方法.ppt

* * Fig.31 The changes in microbe numbers on the metal surface with the treatment time of ultrasonic vibration . * * 阴极极化与超声振动方法清除微生物膜的特征 阴极极化方法对清洁无膜金属表面有效，能耗低，有益于保持表面长期无膜状态． 超声振动方法对有膜金属表面有效，能耗高，有益于快速清除重附着的微生物膜． 阴极极化＋超声振动组合方法能发挥超声振动快速清除已经附着的微生物膜和阴极极化长期保持清洁表面减缓微生物重新附着．结合使用脉冲技术，能够实现低能耗高效率长期控制微生物附着． * * Fig.32 The changes in open-circuit-potentials of high Mo steel with biofilm formation in natural seawater after alternatively treatment by ultrasonic vibration (35kHz) for 30min and cathodic polarization at -800mV for 6 hours. 6.阴极极化-超声振动控制微生物附着性能评价 * * Fig.33 The changes in open-circuit-potentials of 1Cr18Ni9Ti stainless steel with time in natural seawater after the alternative treatment of 30min ultrasonic vibration and cathodic polarization at -800mV for 2 and 6 hours. * * Table 3 The comparison of recovering time of open-circuit-potentials for different metals and different clearing treatment . 控制方法 恢复时间 电极种类 超声振荡 30min 阴极极化 800mV,6hrs 超声振荡与 阴极极化 联合应用 高钼不锈钢 12小时 110小时 170小时 1Cr18Ni9Ti不锈钢 13小时 95小时 160小时 * * Table 4 The comparison of the recovery time for microbe start to reattach after it was removed from metal surface by different clearing treatment. 控制方法 杀菌剂 机械擦除 超声振荡 (30min) 阴极极化 (-800mV+6hr) 超声振荡阴极极化联合(30min,-800mV +6hr) 恢复时间 1天 1天 0.6天 4.6天 7天 * * 海洋环境微生物附着能够引起不同的金属材料开路电位发生不同的变化.不锈钢电位正移;碳钢和铝电位负移;而铜和钛电位很少变化. 不锈钢电位正移程度与附着微生物数量,重量,膜厚度以及含氮化合物数量具有密切的相关性. 高钼钢和1Cr18Ni9Ti不锈钢开路电位正移与微生物附着数量具有线性关系.根据这一关系建立了检测微生物附着附着活性的电化学传感器. 根据微生物附着数量引起的不锈钢开路电位变化建立了恢复时间参数. 研究了机械清除,杀菌剂清除,阴极极化,超声振动以及阴极极化和超声振动组合控制微生物附着方法. 运用恢复时间参数分别评价了上述5种微生物附着控制方法的性能,并证实阴极极化和超声振动组合技术是控制微生物附着的最经济有效的方法. * * 第九章 结束 环境友好防污涂料：陆生植物桉树叶、生姜、辣椒碱提取物，海洋植物中大叶藻、红藻、孔石莼的化学提取物，海洋动物中的海绵和珊瑚虫的化学提取物； 无锡自抛光防污涂料无毒防污涂料：不含有机锡具有自抛光能力的涂料，是国内外当前开发热点。 仿生防污涂料：类似海豚皮、鲨鱼皮结构，它具有表面高度规则和尺寸合适的微结构，改变表面浸润性，不利于有机体附着，减少附着有效附着点，已被冲掉；仿鲨鱼皮粘液渗出、辣素类；螃蟹分泌生物酶能抑制藤壶石灰虫产生的生物胶的凝固；超疏水仿荷叶（5微纳米乳突和蜡状结构的自清洁结构）防污涂料Lotusan建筑涂料5年仍保持自清洁能力； 低表面能防生物附着涂料：表面能低于2.5 X 10-4N/m，海