烧结钕铁硼产品牌号与性能表.docVIP

烧结钕铁硼产品牌号与性能表： · 剩磁 内禀矫顽力 最大磁能积 工作温度 Br iHc (BH)max Tm Grade KGs T Koe KA/m MGOe KJ/m3 °C N50 14.4-13.8 1.44-1.38 ≥12 ≥955 51-47 408-376 ≤80 N35 11.8-12.4 1.18-1.24 ≥12 ≥955 33-36 264-288 ≤80 N38 12.4-13.0 1.24-1.30 ≥12 ≥955 36-38 288-304 ≤80 N40 12.5-13.1 1.25-1.31 ≥12 ≥955 38-40 302-318 ≤80 N42 12.9-13.5 1.29-1.35 ≥12 ≥955 40-42 318-336 ≤80 N45 13.2-13.8 1.32-1.38 ≥12 ≥955 42-46 336-360 ≤80 N48 13.9-14.2 1.39-1.42 ≥12 ≥955 46-48 368-382 ≤80 38M 12.4-12.8 1.24-1.28 ≥15 ≥1194 36-38 288-304 ≤100 40M 12.5-13.1 1.25-1.31 ≥15 ≥1194 38-40 302-318 ≤100 42M 12.8-13.5 1.28-1.35 ≥15 ≥1194 40-42 318-336 ≤100 45M 13.5-14.1 1.35-1.41 ≥15 ≥1194 42-45 336-360 ≤100 47M 13.8-14.1 1.38-1.41 ≥15 ≥1200 45-47 358-376 ≤100 35H 11.7-12.4 1.17-1.24 ≥17 ≥1353 34-36 264-288 ≤120 38H 12.3-12.8 1.23-1.28 ≥17 ≥1353 36-38 288-304 ≤120 40H 12.8-12.9 1.28-1.29 ≥17 ≥1353 38-40 302-318 ≤120 42H 12.9-13.5 1.29-1.35 ≥17 ≥1353 40-42 318-336 ≤120 33SH 11.3-11.8 1.13-1.18 ≥20 ≥1592 31-33 247-263 ≤150 35SH 11.7-12.4 1.17-1.24 ≥20 ≥1592 32-36 264-288 ≤150 38SH 12.2-12.8 1.22-1.28 ≥20 ≥1592 36-38 288-304 ≤150 30UH 10.9-11.6 1.09-1.16 ≥25 ≥1990 29-31 231-247 ≤180 33UH 11.5-11.7 1.15-1.17 ≥25 ≥1990 31-33 247-263 ≤180 35UH 11.7-12.2 1.17-1.22 ≥25 ≥1990 33-36 264-288 ≤180 30EH 10.8-11.2 1.08-1.12 ≥30 ≥2387 29-31 231-247 ≤200 33EH 11.4-11.7 1.14-1.17 ≥30 ≥2387 31-33 247-263 ≤200 35EH 11.7-12.2 1.17-1.22 ≥30 ≥2387 33-36 264-288 ≤200 内禀矫顽力 　　内禀矫顽力（Hcj） 　　单位为 奥斯特（Oe）或安/米（A/m） 　　使 磁体的 磁化强度降为零所需施加的反向磁场强度，我们称之为内禀矫顽力。内禀矫顽力是衡量磁体抗 退磁能力的一个 物理量，是表示 材料中的磁化强度M退到零的 矫顽力。在磁体使用中，磁体矫顽力越高，温度稳定性越好。 最大磁能积 　　(BH)max 退磁曲线上任何一点的B和H的乘积即Bm、 Hm和（BH）代表了磁铁在气隙空间所建立的磁能量 密度，即气隙单位体积的静磁能量，由于这项能量等于磁铁Bm与Hm的乘积，因此称为 磁能积，磁能积随B而变化的关系曲线称为磁能曲线，其中一点对应的Bd和Hd的乘积有最大值，称为最大磁能积。 剩磁 　　retentivity 　　剩余磁化强度的简称。符号Br。磁记录材料内被记录的信息都是作为剩余 磁通被保存下来的。从提高 磁带输出的观点来看，希望Br要尽可能大一些。 　　顽磁，一个物质的顽磁是其剩磁所能达到的最大值。（The retentivity of a substance is the maximum value which the residual flux density can attain.)