偏高岭土对混凝土性能影响研究.pdfVIP

2011年第5期 混凝土与水泥制 品 2011 No5 5月 CHINA CONCRETE AND CEMENT PRODUCTS Mav 偏高岭土对混凝土性能影响研究 杨凤玲 ，嵇银行 ，李玉寿 ，阎晓波 (1．盐城工学院江苏省生态环境材料重点实验室224051；2．江苏省建筑科学研究院 江苏博特新材料有限公司，南京210009) 摘 要：采用偏高岭土、粉煤灰和矿渣等量取代水泥，并将偏高岭土与粉煤灰、矿渣分别复掺配制混凝土，对混 凝土的工作性、抗压强度和耐久性进行了研究。结果表明，偏高岭土用作混凝土掺合料且掺量合理时，其对混凝土坍 落度和抗压强度的影响优于粉煤灰和矿渣，配制的混凝土抗腐蚀性和抗冻融性均有所提高。 关键词：偏高岭土；混凝土；坍落度；抗压强度；耐久性 Abstract：Using the metakaolin，fly ash and slag equivalently replacing cement，and using the metakaolin respec- tively mixing with the fly ash and slag，the specific concrete are prepared．And the workability，compressive strength and durability of concrete are studied．Test resuhs show that，when the metakaolin is used as concrete admixture and the dosage is reasonable，the effects of metakaolin on slump and compressive strength of concrete are better than the effects of ly ash and slag，and the COl~OSiOn resistance and freezing—thaw resistance of concrete are improved．f Key words：Metakaolin；Concrete；Slump；Compressive strength；Durability 中图分类号：TU528 文献标识码：A 文章编号：1000—4637(2011)05—04—05 O 前言 细集料：普通河砂，级配合格，细度模数为2．5， 配制高强和高性能混凝土需要水泥、砂、石、 属Ⅱ区中砂，含泥量1．1％。 水、高效减水剂和矿物掺合料等材料，其中矿物掺 粗集料：普通碎石，连续级配合格，粒径为5— 合料又称为辅助胶凝材料，是高性能混凝土不可缺 31．5mm，压碎值7．9％。 少的第六组分【l_。掺合料既可取代部分水泥，降低成 粉煤灰：干排Ⅱ级灰，其物理性能见表2。 本，又可降低温升，改善工作性能，增加后期强度， 表2 粉煤灰的物理性能 还可改善混凝土的内部结构，提高耐久性闭。常用的 混凝土掺合料大多是具有一定活性的固体工业废 渣，如硅灰、矿渣、粉煤灰等。近年来，高活性偏高岭 土是国内外水泥及混凝土领域重点研究的新一代 矿渣：南京某水泥厂提供，其物理性能见表3。 混凝土矿物掺合料 明。本文以偏高岭土、粉煤灰和