减少帘线钢夹杂物操作技术与实践 谢明泉　刘俊 （武汉钢铁集团公司条材总厂一炼钢分厂，湖北 武汉 430083） 摘 要：简要阐述帘线钢的质量要求，重点分析了帘线钢的生产工艺流程及冶炼和精炼技术现状。从夹杂物形态、尺寸及成分等方面分析了帘线用钢夹杂物的控制技术。生产过程中采用Si、Mn 合金进行终脱氧，结合碱度1.0 左右的精炼渣，以及冶炼过程避免采用铝等措施，夹杂物控制可以满足帘线用钢质量要求。 关键词：帘线钢；夹杂物；氧化铝 中图分类号： TF703 文献标志码：A 文章编号： The Operating techniques and Practice of the Tyre Cord Steel Inclusions in WISCO Xie Mingquan Liu Jun （No.1 Steel-making Plant of General Wire Rod Mill, WISCO, Wuhan 430083 China） Abstract：The quality requirement of tyre cord steel was introduced and the production process was presented, the technical status quo of smelting and refining of tyre cord steel were analyzed emphatically. Inclusion controlling technique to tire cord steel is analyzed from inclusion morphology, size and composition in this paper. In the actual production process, inclusion controlling can satisfy the quality requirement of tire cord steel by applying Si, Mn to the steelmaking final deoxidation, using refining slag with the alkalinity around 1.0 and avoiding adopting aluminum in the refining process etc. Key words: Tyre Cord Steel; Inclusions; Al2O3 0 引言 钢丝帘线，俗称帘线钢，是橡胶制品尤其是汽车子午胎理想的骨架材料。帘线钢是优质硬线钢的精品，是超洁净钢的代表产品和钢铁企业线材生产水平的标志性产品，也是商用钢中强度最高的钢。它在生产中对冶炼、轧制、加工等每个环节都有特殊的要求，是不折不扣的全过程精品钢材。生产帘线钢技术含量极高，被誉为“线材中的极品”、“线材皇冠上的明珠”。 一般来说，钢帘线需要拉到Φ0.38mm以下，拉的越细，生产难度越大。因此能拉到的最小线径是衡量一个钢厂帘线钢生产水平的重要标准。我国钢厂帘线钢大多能拉到Φ0.22mm左右，只有武钢、兴澄特钢等少数几家试拉Φ0.175mm成功。目前，据我所知，我国可以生产帘线钢的钢厂主要有：宝钢、武钢、鞍钢、首钢、沙钢、青钢、邢钢、兴澄特钢等。 欧洲、巴西等一些钢厂拉到Φ0.15mm没有问题。而日本神户则可以拉到Φ0.08mm以下，Φ0.08mm，这是一个非常可怕的数字。我们人类的头发一般直径在Φ0.18mm左右，也就是说，神户拉的钢帘线要比我们头发细一半以上。拉到如此细丝，任何稍大尺寸的硬性夹杂、偏析、非常规组织、内部及表面缺陷都可能是致命的，都可能造成断丝，可见生产难度之高。帘线钢盘条对化学成分、偏析、脱碳层、晶粒度、组织、表面质量、内部缺陷等都有非常严格的要求，近乎苛刻。 1 帘线钢的质量要求 帘线钢是洁净钢的主要代表钢种之一，在拉拔成丝后直径为0.15～0.38mm，其质量取决于帘线用钢坯的质量及帘线盘条性能和质量。因而生产帘线钢对钢中夹杂物、硫化物要求十分严格，而且氮含量必须尽可能地低，对夹杂物的大小、形状和可变形性也提出了很高要求。对各残余元素、连铸坯表面和内在质量缺陷也有严格的要求。目前国际上对于帘线钢夹杂物评价最常用的为皮拉利标准： 第一，夹杂物数量一般要求控制在小于1000个/cm2；第二，夹杂物最大尺寸要求直径小于15μm；第三，不允许有纯Al2O3，氧化物夹杂中Al2O3含量应少于50%；第四，要求钢中总氧含量≤30ppm。 实际上，皮拉利标准仅仅是对帘线钢夹杂物水平的最基本要求，实际上，对于目前帘线钢生产厂家来讲，对夹杂物尺寸的要求