等离子体热负荷协同作用下氖对钨中氘滞留及起泡行为的影响研究课件.ppt

* Summary and outlook Effects of pure Ne and Ne seeding on surface modification Grain orientation dependence sputtering. Sputtering yield: {111}{110}{001}. Ne pre-irradiation suppresses D blistering. (The underlying mechanism will be clarified by further analyses.) Synergetic effect with D: blister cracking Effects of Ne seeding on D retention D concentration decreases in the near-surface (blister cracking), and increases in the bulk after exposure to mixed plasma (improved diffusion). Additional release peaks appear at higher temperatures (additional types of D-traps), which is probably due to the synergetic effect of Ne and D irradiation, and total D retention increases. Ne and Ar exhibit similar effects on D behaviors in W. * Summary and outlook Performances of rolled W exposed to combined D-Ne mixed plasma and transient heat loads Successive transient heat loads and mixed D-Ne plasma exposures result in similar local surface morphology compared to only plasma exposures. Simultaneous transient heat loads and mixed D-Ne plasma exposures result in cracking and local melting of the blister caps. Transient heat loads results in an increase of the D retention in the sub-surface. Ne seeding reduces the D retention in the sub-surface (~ 4 μm) under successive and simultaneous transient heat loads and plasma exposures. TDS measurements are required and will be carried out in future. * * D+Ne mixed plasma Exposure temperature: ~450 K Incident ion energy: ~40 eV Ion flux: 0.9-1.2 E22 D/m2s Ne-ion ratio: 0, 10% D fluence: 1E26 D/m2 Side manipulator sample holder Grains are elongated parallel to plasma loads. 1 μm Surface morphology ITER-grade W Mixed D-Ne plasma exposures of ITER-grade W * the line-integrated ionization flux, which is observed perpendicular to the plasma column with the imaging spectrometer. Ionization per photon coefficient, S/XB-factor gives the number of ionizations per photon for a single spectral line ADAS database. (neutral Ne 668nm) the ax