聚合物纳米复合材料69页文档.ppt

聚合物共混改性原理 Comparison of the Youngs modulus of clay/nylon -6 nanocomposites and glass fiber reinforced nylon-6 composites with low filler loading Fengge Gao, materials today,2019,50-55 In the low filler loading range, clay/polymer nanocomposites have the potential to replace traditional fiber reinforced composites. 聚合物共混改性原理 Modulus increase by layered silicate reinforcement of PA66 L. A. GOETTLER, Polymer Reviews, 47:291 – 317, 2019 普通层状 填料 玻纤增强 聚合物共混改性原理 (a) Organoclay (OMSFM) (wt %) dependence of HDT of neat PLA and various PLACNs. (b) Load dependence of HDT of neat PLA and PLACN7 Thermal properties Suprakas Sinha Ray, et al, Chem. Mater. 2019, 15, 1456-1465 聚合物共混改性原理 TGA analysis of PDMS(solid line).and PDMS nanocomposite(dashed line)(mass fraction 10% mica-type-silicate, MTS). Lines were added to indicate 50% mass loss. Burnside, S.D., Giannelis, E.P., Chem. Mater. 2019. 7, 1597 聚合物共混改性原理 Comparison of the Heat Release RateHRR. plot for nylon-6, nylon-6 silicate- nanocomposite(mass fraction 5%)at 35 kW/m2 heat flux, showing a 63% reduction in HRR for the nanocomposite. flame retardant Jeffrey W. Gilman, Applied Clay Science, 15, 2019.31 – 49 放热速率 显著下降 聚合物共混改性原理 PP 及其纳米复合材料的热释放速率对比 （热通量 =35kW/m 2 ) 聚合物共混改性原理 Flammability performance for nylon-6 nanocomposites nanocomposite works with other flame retardants in a synergistic or cooperative manner to lower the polymer flammability (heat release rate) Comparison between nanocomposites and conventional flame retardants Alexander B. Morgan, Polym. Adv. Technol. 2019; 17: 206 – 217 工业上评价材料阻燃性 能的检测标准 聚合物共混改性原理 Beyer, G., 2019 Nanocomposite Power Cable Kabelwerk Eupen 聚合物共混改性原理 Selected video images at 100, 200, and 400 s in nitrogen at 50 kW/m 2 . Takashi Kashiwagi, Polymer 45 (2019) 881 – 891 Mechanism: The silicate-rich char acts as an excellent insulator and mass transport barrier ,thereby reducingthe heat r