年产5万吨铝锭连铸生产线设计.docVIP

摘 要：本设计以国内外铝锭连铸生产实践为基础，结合我国近几十年来铝锭连铸生产的新工艺，对铝锭连铸整条生产线做了的设计。铝锭型设计参考了加拿大锭型，同时也参照了日本锭型，并对铝锭的质量做了计算。机架的设计是参考了L D S—20—F型2 0 k g铝锭铸造机设计的，同时还配备有冷却池、机械手、码垛机等设备。本连铸机从浇铸到码垛完全机械化，大大提高了生产效率。混合炉的设计是根据铝锭连铸机的生产能力选取的，使整条生产线能够连续的运转。车间采用先进的环保屋顶通风设备。 关键词：铝锭 连铸机 混合炉 Abstract：The design practice of continuous casting of aluminum ingots at home and abroad, combined with the continuous casting of aluminum ingots produced in China in recent decades, new technology, on the whole production line of aluminum ingot casting design done.?Design reference ingot in got of Canada, while also drawing on the Japanese ingot, and the quality of aluminum ingots was calculated.?Rack is designed with reference to LDS —20—F Type 2 0 kg aluminum ingot casting machine, and continuous casting machine is also equipped with cooling pond, manipulator, stacking machines and other equipment.? Fully mechanized tacking from casting to greatly improve the efficiency of production.?Mixing furnace design is based on aluminum ingot casting machine capacity selected, so that the entire production line can run continuously. Green roof workshop advanced ventilation. Keywords: Aluminum ingot Caster Mixing furnace 第一章 文献综述 1.1国内外铝工业概况 1.2铝锭连铸技术发展 近50年来，铝连续铸造在世界铝工业中的地位变得越来越重要，铝连续铸造发展的驱动力是,与传统铸块热轧工艺相比,铝连续铸造工艺在经济上占优势；连续铸造工艺技术投资较低;耗能低；劳动力成本低; 因此加工成本也低。许多年来，人们一直认为铝连续铸造工艺技术在经济上的优势仅适用于那些产量低的工厂，但最近的较精确的研究结果表明,铝连续铸造工艺技术的成本节省适用于各类工厂，铝连续铸造工艺技术的投资成本总是比传统的铸块热轧工艺技术低，这是已经经过实践证明了的。 1.3 铝连续铸造机类型 （1）瑞铝Ⅱ型连续铸造机 （2）带式连续铸造机 （3）加铝双带铸造机 （4）双辊铸造机 1.4铸锭方法分类 1.4.1铝的连续铸锭法 1.4.1.1静模铸造 ⑴ 立式半连续铸锭 （2）热顶铸造 ⑶水平连续铸造 1.4.1.2动模铸造 ⑴ 辊间铸造 ⑵ 轮间铸造 ⑶ 带间铸造 ⑷ 无接触铸造 1.4.2不连续铸锭法 ⑴ 锭模铸造 ⑵ 沉浸铸造 ⑶ 普通原铝铸造 1.5 连铸工艺 混合炉浇铸，首先要经过配料，然后倒人混合炉中，搅拌均匀，再加入熔剂进行精炼。浇铸合金锭必须澄清30分钟以上，澄清后扒渣即可浇铸。 浇铸时，混合炉的炉眼对准铸造机的第二、第三个铸模，这样可保证液流发生变化和换模时有一定的机动性。炉眼和铸造机用流槽联接，流槽短一些较好，这样可以减少铝的氧化，避免造成涡旋和飞溅，铸造机停用48h以上时，重新启动前，要将铸模预热4h。铝液经流槽流入铸模中，用铁铲将铝液表面的氧化膜除去，称为扒渣。流满一模后，将流槽移向下一个铸模，铸造机是连续前进的。铸模依次前进，铝液逐渐冷却，到达铸造机中部时铝液已经凝固成铝锭，由打印机打上熔炼号。当铝锭到达铸造机顶端时，已经完全凝固成铝锭，此时铸模翻转，铝锭脱模而出，落在冷却水池中