剃齿刀热处理工艺试验.doc

剃齿刀热处理工艺试验 摘要：本课题是对剃齿刀的生产材料-M2系列高速钢的热处理工艺进行研究，课题来源于太原工具厂。对M2高速钢热处理工艺的研究，主要是通过淬火、回火以及高温回火试验，研究一种正确的热处理工艺方法，以使其能达到剃齿刀生产要求的高回火温度和高红硬性。同样，正确的热处理对于一种刀具的经济性也有着决定性的意义。 关键词：剃齿刀，M2高速钢，热处理工艺 Heat treatment process test of the shaving cutter Abstract ：his topic is the study Production of shaving cutter?material of M2 high speed steel series of heat treatment process, topic is from the Taiyuan tool factory. Study of M2 high speed steel heat treatment process, mainly by quenching tempering and high temperature tempering test, study a method to correct heat treatment process, So that it can?reach the?shaving cutter?production requirements of the?high tempering?temperature and?high hardness. Also, the correct heat treatment to a tool of economy also has a decisive significance. Keywords: Gear shaver, M2 high speed steel, heat treatment process 目 录 30464 1 绪 论 1 26701 1.1 课题的背景及意义 1 20470 1.2 高速钢的发展及应用状况 2 2430 1.2.1 国外高速钢的发展状况 2 25039 1.2.2 我国高速钢的发展状况 3 1749 1.2.3 质量水平与国外相比 5 6086 1.3 高性能高速钢的发展及特点 6 1817 1.4 高速钢的组织特点 8 11291 1.5 本课题的研究内容 9 6104 2 剃齿刀的加工原理及问题 10 26948 2.1 齿轮加工工艺简介 10 2120 2.2 剃齿原理 10 15827 2.3 剃齿加工原理 11 16413 2.4 剃齿刀的加工 11 108 2.4.1 刀具磨损 12 6693 2.4.2 刀具破损 12 27772 2.5 失效分析与常见热处理缺陷 14 18598 3 M2高速钢的组织性能特点 16 25997 3.1 M2高速钢的成分特点 16 3.1.1 钨在钢中的影响 15989 16 3.1.2 钼在钢中的影响 25824 17 3.1.3 铬在钢中的影响 15989 17 3.1.4 钒在钢中的影响 25824 18 3.1.5 碳在钢中的影响 25824 18 4 试验条件与方法 15989 19 4.1 试验材料 25824 19 4.2 试样编号 25824 20 4.3 试验仪器与设备 15989 20 4.3.1 淬火工艺设备 25824 20 4.3.2 回火工艺设备 25824 21 4.3.3 其他各种设备 15989 21 4.4 工艺试验方法 25824 21 4.4.1 淬火工艺试验方法 25824 21 4.4.2 回火工艺试验方法 15989 22 4.4.3 高温回火工艺试验 25824 23 4.5 淬火工艺曲线的确定 25824 24 5 试验结果与分析 15989 26 5.1 M2淬火组织观察 25824 26 5.1.1 M2淬火组织金相检验 25824 26 5.1.2淬火组织金相图片 15989 26 5.1.3 碳化物的分布 25824 28 5.1.4 奥氏体晶粒大小 25824 28 5.1.5 M2淬火试样硬度测定结果与分析 15989 29 5.1.6 淬火组织分析 25824 30 5.2 M2高速钢试样回火硬度的检验 25824 31 15989 5.3 淬火温度对红硬性的影响 32 25824 5.3.1 各检测温度处理后基体的硬度 33 25824 5.3.2 高温回火前后硬度变化 33 30986 结 论 34 6