JOIN LEADER 108 Polymer-Modified Cementitious Waterproofing Coating TDS 防水胶浆分析和总结.docxVIP

Technical Data Sheet Revision Date: 25/Aug/2011 JOIN LEADER 108 Polymer-Modified Cementitious Waterproofing Coating JOIN LEADER 108 Polymer-Modified Cementitious Waterproofing Coating PRODUCT DESCRIPTION PRODUCT DESCRIPTION JOIN LEADER 108 Polymer-Modified Cementitious Waterproofing Coating is a cement based, 2-component, polymer-modified flexible waterproofing coating. The 2-components of JOIN LEADER 108 Polymer-Modified Cementitious Waterproofing Coating react chemically after mixing to form a hard and elastic film which bonds tenaciously to most concrete or masonry substrate to protect against possible ingress of water. Complied with the requirement of GB/T 23445-2009, Type II. FEATURES FEATURES Good crack bridging capability (up to 1 mm at 20°C) Can be used on wet or dry surface Good adhesion to sound substrates 1 Impermeable Increased frost and salt resistance Anti-carbonation protection Non-toxic, same as cement Flexible Resistant to freezing thawing (-10°C) Economic Pre-batched components Mixes and applies easily Easily applied by rollers or brushes TECHNICAL TECHNICAL DATA As Supplied –tested at 23℃±2℃, RH50%±5%: Aspect: Component A: White Latex Component B: Dark Green Powder Specific Gravity: A+B (mixed) = 1.7 kg/L Pot life, min: 30 Remark: The directives contained in this documentation are the result of our experiment and of our experience and have been submitted in good faith. Because of the diversity of the materials and substrates and the great number of possible applications which are out of our control, we cannot accept any responsibility for the results obtained. In every case it is recommended to carry out preliminary experiments. JOIN LEADER ADHESIVE CO., LTD. Technical Data Sheet Revision Date: 25/Aug/2011 Foot Trafficable, Hour 2~3 Application Temperature, ℃: +5 to +40 As Supplied – tested at 23℃±2℃, RH50%±5% 14 days : Service Temperature, ℃: -40~+250 Solid Content, % 75 Tensile Strength, MPa: 2.4 Adhesion Strength, MPa 0.9 Elongation at Bre