熏烟热处理技术在国内及日本的发展与应用研究.pdfVIP

熏烟热处理技术在国内及日本的发展与应用研究 摘要：介绍了熏烟热处理窑的结构以及熏烟热处理技术的定义、特点及其基础理论，并对日本应用熏烟热处理技 术在日本落叶松（Larix kaempferi ）、日本冷杉（Abies firma ）、油棕（Elaeis gunieensis ）以及速生材柳杉（Crypto- meria fortunei ）等方面所做的研究进行了概括；对熏烟热处理后的木材尺寸稳定性、耐久性、物理力学性能的改 善进行了综述；对我国应用熏烟热处理技术在竹炭生产以及杨木胶合板方面所做的初步研究进行了介绍，并对熏 烟热处理技术未来的发展方向和在我国的发展空间进行了展望。 关键词：熏烟热处理窑；熏烟热处理；速生材；木材干燥 中图分类号：S781.7 文献标识码：A Research and Utilization of Smoke Heating Treatment Technology in China and Japan Abstract: Presentation was made on the structure of smoke heating treatment furnace as well as on the definition, characteristics and the related fundamental theory of smoke heating treatment technology. Summaries were carried out on application of the technology in Japan to wood of Japanese larch(Larix kaempferi ), Momi fir(Abies firma) , Oil palm(Elaeis gunieensis) and Japanese cedar(Cryptomeria japonica). Description was conducted on improvement of dimensional stability, durability, and physical properties of the wood processed by smoke heating treatment technology, including preliminary research on applying this technology to bamboo charcoal production and poplar plywood in China. Prospects of smoke heating treatment technology in China were described. Key words: smoke heating treatment kiln; smoke heating treatment technology; fast-growing trees; wood drying 近年来我国胶合板工业发展迅速，但与此同时，胶合板的原料问题也变得十分突出，特别是柳桉、椴木、 水曲柳等天然林木材日益减少，无法满足实际生产的需要。解决胶合板原料问题的有效途径就是合理利用人工 林速生材。杨树、杉树、桉树等均为我国主要的速生材树种[1] ，杨树因其适应性强、生长快、材质白等独特的 优势已成为我国胶合板的原料树种之一。但由于杨树木材存在着易变形、易开裂、强度低等质量缺陷[2] ，基本 只用于生产胶合板，而不能用于制材加工，严重制约了其利用范围。对杨木材性的研究表明，除生长应力之外， 杨木含水率沿树干方向分布不均匀，干燥时低含水率部位首先水分蒸发到纤维饱和点，并开始干缩，在木材内 形成干缩应力。而高含水率部位干燥到达纤维饱和点所需时间较长，这种应力形成的时间差最后造成干燥后的 板面不平整，翘曲变形严重，一当板面受压时并发生破裂现象。 收稿日期：2010-03-11 ；修回日期：2010-07-08 作者简介：刘丽丽（1984 －），女，山东菏泽人，硕士，从事人造板加工研究；*通讯作者。 5 期 刘丽丽，等：熏烟热处理技术在国