螺栓加工工艺（Boltprocessingtechnology）.docVIP

螺栓加工工艺（Bolt processing technology） 螺栓加工工艺(Bolt processing technology) Therefore, mechanical descaling is affected by iron sheet thickness, structure and stress state. It is used for carbon steel wire rods of low strength fasteners (less than or equal to grade 6.8). High strength fasteners (greater than or equal to 8.8) wire rod, after mechanical descaling, in order to eliminate all the iron oxide, and then through the chemical pickling process, that is, complex descaling. For low carbon steel wire rod, mechanical descaling residual iron easy to cause uneven wear particle pattern. When the particle hole of the wire rod drawing friction when the outside temperature on the adhesion sheet, make wire rod steel wire surface longitudinal grain mark, wire rod for cold heading bolt flange or cylinder head screws, head of micro cracks, more than 95% is produced in the process of drawing steel wire surface scratches caused by. Therefore, mechanical descaling is not suitable for high-speed drawing. Four, drawing process has two purposes, one is the reform of raw material size; two is through the deformation strengthening effect of the fastener to obtain the basic mechanical properties, for medium carbon steel, carbon steel and a purpose, which is the lamellar cementite obtained after controlled cooling in the wire drawing process as may Crack, for subsequent spheroidizing annealing (softening) to prepare granular cementite. However, some manufacturers in order to reduce the cost of drawing passes arbitrarily reduced, large reduction rate increases the work hardening of steel wire rod tendency, directly affects the performance of steel wire rod for cold heading. If the distribution of the reduction ratio of each pass is not appropriate, the torsion of the wire rod and the steel wire will be produced during the drawing process, and the longitudinal crack along the steel wire will be exposed in the cold heading process of the steel wire. In addition, during the drawing process,