流变性对高早强泡沫混凝土性能的影响.pdfVIP

2023年第7期 混凝土与水泥制品 2023 No.7 7月 CHINA CONCRETE AND CEMENT PRODUCTS July 流变性对高早强泡沫混凝土性能的影响 凌建祥1,董波1,叶焕2*,韩意² 摘要：为降低泡沫混凝土生产过程中的能耗，改善泡沫混凝土的性能，研究了流变性对高早强免蒸压泡沫混凝 土发气效果和硬化后性能的影响。结果表明：当屈服应力超过200Pa后，泡沫混凝土不再膨胀；高早强免蒸压泡沫混 凝土的6h抗压强度可以达到2.7MPa,导热系数基本不大于0.20W/(m·K) ；浆体的屈服应力偏小可能导致孔隙率 （体积密度）相近的泡沫混凝土导热系数相差30%，抗压强度相差100%左右。 关键词：流变性；免蒸压；泡沫混凝土；导热系数 中图分类号：TU528.2 文献标识码：A doi:10.19761/j.1000-4637.2023.07.070.05 Effect of rheological properties on the performance of high early strength foamed concrete LING Jianxiang, DONG Bo, YE Huan?*, HAN Yi? (1.Bengbu Architectural Design and Research Institute Group Co., Ltd., Bengbu 233000, China; 2.Anhui Science and Technology University, Bengbu 233000, China) Abstract: In order to reduce the production energy consumption and improve the performance of foamed concrete, the effect of rheological properties on gas generation and hardening properties of high early strength non-autoclaved foamed concrete was studied. The results show that the foamed concrete no longer expands when the yield stress exceeds 200 Pa. The 6 h compressive strength of high early strength non-autoclaved foamed concrete can reach 2.7 MPa, while the thermal conductivity is no more than 0.20 W/(m·K). The lower yield stress can lead to a 30% difference in thermal conductivity and a 100% difference in compressive strength for foamed concretes with similar porosity (or volume density). Keywords: Rheological property; Non-autoclaved; Foamed concrete; Thermal conductivity 0引言 随时间的变化。近年来，越来越多的研究者通过流 节能降碳是当前建筑行业发展的大趋势。为 变性研究浆体的早期性能，结果表明，该方法更有 了减少建筑使用过程由制冷和供暖产生的能耗和 利于对泡沫混凝土的孔结构进行控制[2-4]。使用高早 碳排放，泡沫混凝