(2877)--初始长度测量时间对自流平砂浆尺寸变化率测试结果影响研究_.pdfVIP

检验与认证 初始长度测量时间对自流平砂浆尺寸变化率测试结果影响研究 Study on influence of initial length measurement time on measurement result of size change rate of self-leveling mortar 摘要：自流平砂浆可以在几小时后终凝并产生高强度，其终凝之后至养护24h之间的收缩具有很高的研究价值。本 文通过平行实验分别研究自流平砂浆在终凝之后脱模、在抗压强度达到10MPa之后脱模和在24h龄期之后脱模的 尺寸变化率，研究自流平砂浆初始长度测量时间对尺寸变化率的影响。结果表明，自流平砂浆终凝之后脱模并测 量初始长度时尺寸变化率最大，24h龄期之后脱模并测量初始长度时尺寸变化率最小，且尺寸变化率随养护龄期的 增加而增大，增速越来越小。 关键词：自流平砂浆；尺寸变化率；初始长度；凝结时间 Abstract : Self-leveling mortars can solidify in hours and get high strength, therefore, the shrinkage of self-leveling mortar between final solidification to 24h curing is of great research value. In this paper, through parallel experiments, the size change rates of self-leveling mortar demoulding after final setting, demoulding after the compressive strength reaches 10MPa and demoulding after 24h were respectively measured, and the effect of measuring time of initial length of self- leveling mortar on size change rate was studied. The results show that the size change rate of the initial length measured by demoulding immediately after the final setting of self-leveling mortar was the highest, and the size change rate of the initial length measured by demoulding after 24h was the lowest. The size change rate increased with the increase of curing age, but the growth rate became smaller and smaller. Keywords: self-leveling mortar; rate of size change; initial length; setting time 中图分类号：TU528　文献标志码：B　文章编号：1003-8965（2020）02-0001-03 0　引言 1　试验 自流平砂浆具有非常好的流动性，直接浇筑在地面上 1.1　试验方案 可以自动流平，并在数小时后产生很高的强度。该材料以 本文通过三种方法确定初始长度测量时间点，三组试 流平性好、早期强度高、铺设简易、施工快速、稳定性好等 验编号分别为 1#，2# ，3#。1#试验以砂浆终凝 30min 的时 优点，广泛应用于工业、商业、家装等领域[1-2] 。目前，人们 间作为初始长度测量时间，2#试验以砂浆抗压强度达到 对地坪材料性能的要求