刘海深，等：白泡石提铝降钾可行性技术实验研究 技术研究 + 中图法分类号：TQ171.77 4      文献标志码：A 白泡石提铝降钾可行性技术实验研究 刘海深，罗大芳，许绍彬，王利明 （重庆国际复合材料股份有限公司，重庆 400082） 摘  要：对重庆永川某白泡石中高岭土、石英、云母及长石进行了分离实验研究，结果表明 ：白泡石干法磨矿后，过 120 目细 筛即可有效分离部分石英，达到提高铝质量分数的目的，铝质量分数能达到 18.48%，云母也富集于筛下物中，导致钾质量分 数上升至 2.18%，需要通过浮选手段进行分离，浮选后的精矿产品铝质量分数为 17.25%，钾质量分数为 0.76%。 关键词：白泡石 ；提铝 ；降钾 ；云母 ；高岭石 ；浮选 Experimental Study on the Feasibility of Increasing Aluminum and Decreasing Potassium from White Afrodite Liu Haishen, Luo Dafang, Xu Shaobin, Wang Liming ( Chongqing Polycomp International Corp., Chongqing 400082 ) Abstract: In this paper, a test of separating kaolin, quartz, mica and feldspar in white afrodite in Yongchuan, Chongqing was carried out. The results showed that after the dry grinding of white afrodite, part of quartz could be effectively separated after passing through a 120-mesh fine sieve to increase the aluminum content. The aluminum content could reach 18.48%, but mica was also enriched in the throughs, causing the potassium content to rise to 2.18%. It needed to be separated by flotation. The aluminum content in the concentrate product after flotation was 17.29%, and the potassium content was 0.76%. Key words: white afrodite; increase of aluminum; decrease of potassium; mica; kaolinite; flotation 0  前言 铝原料之一。目前，玻纤生产所用白泡石的铝元素 重庆砂岩资源丰富，主要分为软质砂岩、硬质石 的质量分数（本文均以氧化物计）约为 10%~12%， 英砂岩、硬质白泡石砂岩3种。其中白泡石砂岩是一 必须加入一定量高岭土、叶蜡石或其他高铝矿物，才 ［4，5］ 种高岭土胶结石英晶粒的沉积岩，具有一定的力学强 能达到玻纤对铝元素质量分数要求 ，但满足玻 ［1-3］ 度，广泛应用于建筑、耐火材料、建材等领域 。