微晶白云母的表面修饰及其与核-壳型ACR共同改性PVC材料的研究的中期报告.docxVIP

微晶白云母的表面修饰及其与核-壳型ACR共同改性PVC材料的研究的中期报告 摘要： 本研究采用表面修饰技术，对微晶白云母进行改性处理，并将其与核-壳型ACR共同改性PVC材料进行研究。首先对微晶白云母进行表面修饰，采用辛烯基硅烷（KH570）进行表面修饰，通过FTIR分析表面修饰效果良好，表面官能团明显增加。然后将微晶白云母与核-壳型ACR进行共同改性PVC材料的制备。通过DSC、TGA、SEM等多种分析手段对改性PVC材料进行表征和分析。结果表明，微晶白云母与ACR共同改性的PVC材料的热稳定性、力学性能和耐候性能有明显提高。在共同改性PVC材料中，微晶白云母与ACR的质量比为1:1时，PVC材料的力学性能达到最优。 关键词：微晶白云母，表面修饰，核-壳型ACR，共同改性PVC材料 Abstract: In this study, surface modification technology was used to modify microcrystalline white mica, and it was studied jointly with core-shell ACR to modify PVC materials. First, surface modification was carried out on microcrystalline white mica, and octenylsilane (KH570) was used for surface modification. The surface modification effect was good, and the surface functional groups increased significantly as analyzed by FTIR. Then, microcrystalline white mica and core-shell ACR were used to modify PVC materials. The modified PVC materials were characterized and analyzed by DSC, TGA, SEM and other methods. The results showed that the thermal stability, mechanical properties and weather resistance of PVC materials modified by microcrystalline white mica and ACR were significantly improved. In the joint modification PVC materials, the mass ratio of microcrystalline white mica to ACR reached the optimal mechanical properties at 1:1. Keywords: microcrystalline white mica, surface modification, core-shell ACR, jointly modified PVC materials