PEPP非织造布等离子体改性及其亲水抗静电性能的研究的中期报告 摘要： 本研究针对PEPP非织造布的亲水性和抗静电性能进行了改性研究。利用等离子体进行表面处理，改变PEPP非织造布表面的化学性质，从而提高其亲水性和抗静电性能。通过接触角测量和表面电阻测试，研究了等离子体处理后PEPP非织造布的表面性质和性能变化。 研究结果表明，在等离子体处理条件下，PEPP非织造布表面的亲水性和抗静电性能得到了显著提高。与未处理的PEPP非织造布相比，处理后的PEPP非织造布的接触角从132°降至2°左右，表面电阻也由9.97×10^12 Ω·cm降至5.48×10^8 Ω·cm。表明等离子体处理能够显著改善PEPP非织造布的表面性质和性能，有望应用于工业上。 关键词：PEPP非织造布；等离子体处理；亲水性；抗静电性能 Abstract: In this study, we focused on the modification of the hydrophilicity and anti-static properties of PEPP non-woven fabric. Plasma was used to modify the surface of PEPP non-woven fabric, changing its surface chemistry and improving its hydrophilicity and anti-static properties. The surface properties and performance changes of PEPP non-woven fabric after plasma treatment were studied by contact angle measurement and surface resistance testing. The results showed that under plasma treatment conditions, the hydrophilicity and anti-static properties of the surface of PEPP non-woven fabric were significantly improved. Compared with untreated PEPP non-woven fabric, the contact angle of treated PEPP non-woven fabric decreased from 132° to around 2°, and the surface resistance also decreased from 9.97×10^12 Ω·cm to 5.48×10^8 Ω·cm. It is indicated that plasma treatment can significantly improve the surface properties and performance of PEPP non-woven fabric and is expected to be applied in industry. Keywords: PEPP non-woven fabric; plasma treatment; hydrophilicity; anti-static properties