硅偶联剂交联壳聚糖纤维的染色性能.docx

硅偶联剂交联壳聚糖纤维的染色性能

何雪梅

【摘要】ACSHandGCSHfiberswereobtainedbythesurfacemodificationofpurechitosanfiberwiththeSiO2nanoparticletreatedrespectivelybyusing3-aminopropyltriethoxysilane(KH550)andy-Glycidoxypropyltrimethoxysilane(KH560)asthecross-linkingagents.Themolecularstructure,micro-surfacemorphologyanddyeingperformanceofthepurechitosan,ACSHandGCSHfiberswereresearchedwithFTIR,SEMandotherindicativemethods.FTIRspectraprovedthatsilicacouplingagentswascrosslinkedwiththechitosanfiberandthenanoSiChparticlesdistributedatthesurfaceofthechitosanfiberbythesurfacemodification.TheoptimizationdyeingparametersforACSHandGCSHfiberwithdirectPink12Bwere20瘵，pHvalueof8,time120minand180minrespectively.ACSHfiberhadthehigherdyeingratethanthatofGCSHfiberforDirectPink12B.TheadsorptionkineticsofACSHandGCSHfibersforDirectPink12Bcanbedescribedbythepseudosecond-orderreactionmodel.%利用3.氨基丙基三乙氧基硅烷(0550)及Y-缩水甘油醚氧丙基三甲氧基硅烷(560)为交联剂,分别制备了纳米SiO2改性壳聚糖纤维ACSH和GCSH.通过红外光谱(FTIR)、扫描电镜(SEM)等表征方法研究了SiO2改性壳聚糖纤维ACSH和GCSH的分子结构和微观形貌,并对其染色性能进行了研究.红外光谱证实硅偶联剂与壳聚糖纤维发生了交联，纳米SiO2粒子分布于改性壳聚糖纤维表面.染色条件为室温、pH值为8,染色时间分别120min、180min时直接桃红12B在ACSH和GCSH纤维上的

上染率较高.与GCSH纤维相比,ACSH纤维用直接桃红12B染色上染率更高.ACSH和GCSH纤维对直接桃红12B的吸附动力学行为可用准二级动力学模型进行描述.

【期刊名称】《丝绸》

【年(卷)，期】2012(000)004

【总页数】5页(P19-23)【关键词】壳聚糖纤维;硅偶联剂;交联;染色性能【作者】何雪梅

【作者单位】盐城工学院纺织服装学院，江苏盐城224003

【正文语种】中文

【中图分类】TS193.8随着人们对自身健康及环境问题的日益关注，生态环保可降解的材料越来越受到人们的欢迎［1-2］。作为自然界唯一带正电荷的再生纤维，壳聚糖由于其化学结构与纤维素类似，具有相当的生物活性、生物相容性、抗菌性、可降解性及其他许多独特的性能，使其在化妆品，农业，食品工业，生物医学，纺织等众多领域得到了广泛的研究及应用［3-8］。然而，作为纺织材料，壳聚糖纤维本身的机械性能比较差，易缩水，干燥后易变形，在酸性条件下的易溶失性等缺陷，限制了其作为纺织纤维材料的进一步应用。为了获得具有理想性能的纤维材料，许多研究者对壳聚糖聚合物进行交联改性［9］。由于有机硅溶胶容易进行各种物理和化学改性，如加入某些添加剂，使添加剂均匀地包覆到三维有机硅金属氧化物的网络结构中。不同的添加剂，如Y-缩水甘油氧丙基三甲基硅烷、3-氨基丙基三乙氧基硅氧烷、乙烯基三乙氧基硅氧烷、异氰酸丙基三乙氧基硅(ICPTES),可获得不同性能的纳米溶胶膜［10-

13］。

本研究通过GPTMS和APTES对纯壳聚糖纤维表面改性，探讨不同硅偶联剂对改性纤维的染色性能及不同的染色条件如染色时间、pH值、温度和染料浓度对纤维染色性能的的影响。

壳聚糖纤维(CS)由青