小型精密结构件的真空油淬研究.pdfVIP

HotWorkingTechnology2019,Vol.48,No.12

小型精密结构件的真空油淬研究

马宇洛，任卫斌，赵金龙，汪建国

(中国空空导弹研究院电装分厂，河南洛471003)

摘要：设计制作了大小两种保温套，将精密小型结构件放入保温套中，进行真空保温和淬火转移试验。结果表明，

小型精密结构件真空油淬可以克服和消除卧式真空油淬炉结构限制问题，零件淬火后，硬度均匀，满足工艺要求。

关键词：真空淬火；转移时间；组织；硬度均匀；保温套

DOI:10.14158/j.cnki.1001-3814.2019.12.036

中图分类号:TG162.7文献标识码：A文章编号:1001-3814(2019)12-0150-03

StudyonVacuumOilQuenchingofSmall-scalPrecisionStructuralMembers

MAYuluo,RENWeibin,ZHAOJinlong,WANGJianguo

(ElectricInstallationPlant,ResearchInstituteofChinaAirborneMissleAcademy,Luoyang471003,China)

Abstract:Twokindsofinsulationsleeveweredesignedandmade.Vacuuminsulationandquenchingtransfertestswere

carriedoutbyplacingthesmall-scaleprecisionstructureintotheinsulationsleeve.Theresultsshowthat,thevacuumoil

quenchingcanovercomeandeliminatethestructurallimitationquestionofhorizontalvacuumoilquenchingfurnace.After

quenching,thehardnessofthepartsisuniform,whichmeetstherequirementsoftheprocess.

Keywords:vacuumquenching;transfertime;microstrucure;hardnessuniformity;insulationsleeve

平衡摆轴、平衡摆销是精密小型结构件,平衡摆批试加工，抽取其中4件零件检测，维氏硬度结果见

销零件尺寸见图lo零件外径仅/0.8mm,尺寸公差表1,其中有不满足工艺要求的硬度(315-412HV)

精度0.040〜0.010mm,装配面粗糙度Ra为0.32〜的情况，且零件之间硬度差异约150HV。

0.8p.mo零件材料为T8A,热处理硬度315〜412表1平衡摆销真空淬火检测硬度(HV)

HV,要求零件在表面处前进行光亮淬火。为此，本Tab.lTesthardnessofbalancpinbyvacuum

quenching(HV)

文采用VOQ2-100卧式双室真空油淬炉进行真空淬要求硬度值试样实测硬度备注

火，以确保零件表面光亮。

315〜412321.364J31.470不合格