研发与应用 研发与应用 张化宾 王瑞真 唐效国 （莱芜钢铁股份有限公司热电厂） 摘 要 波纹补偿器是煤气管网系统中的重要备件，目前煤气管网中的补偿器由于受高炉煤气中酸根离子的影响出 现不同程度腐蚀，通过对补偿器失效分析，确认补偿器失效与其结构、材质和运行工况有关，并从补偿器失效影 因素出发进行改型研发。 关键词 补偿器 酸性腐蚀 254SMO 不锈钢 Research and Application Zhang Huabin Wang Ruizhen Tang Xiaoguo (Thermal Power Plant of Laiwu Steel) Abstract The ripples compensate machine is the important spare parts in the gas pipe net system, the in expiation of machine in the gas pipe net passes to confirm the in expiation of machine expiration to have something to do with its structure,material and circulating the work condition towards compensating the machine expiration analysis, because of being subjected to the sour root in the blast furnace coal gas the influence of the ion to appear different degree corrosion currently, and from compensate machine expiration the influence factor set out to carry on remodeling a development. Key words compensate machine, the acidity decay, 254SMO stainless steel 1 概述 长时间以来，受高炉喷煤工艺、炼铁工序变化和全干法除尘技术应用等影响，高炉煤气中富有的氯离子、 硫酸根离子等形成的复合产物对不锈钢、碳钢等腐蚀严重，造成高炉煤气管网、设备和设施系统性损坏。突 出反映在管道补偿器上相继出现不锈钢波纹管严重点腐蚀穿孔、波纹管与接管环焊道开裂、补偿器内衬导流 筒凸流道处冲蚀等重大隐患，造成在煤气系统上广泛应用的波纹补偿器大量失效和损坏，严重影响了高炉生 产的稳定运行和煤气正常输送，给公司生产经营带来巨大损失。同时，补偿器泄漏后极易造成人员煤气中毒 和煤气燃爆，引发安全事故。受酸性腐蚀影响，原使用的补偿器平均寿命不足8 个月。 为彻底消除这一重大隐患，公司上下高度关注，成立技术攻关小组，热电厂结合现场实际与机动处、制 造厂家、高校科研单位等共同研究、分析，从补偿器不锈钢材质选型、结构制作、工艺改进和采取特殊处理 等方面进行了一系列研发改造，有针对性的、合理的制定出了解决方案，从2006 年4 月～9 月，历时半年 之余成功研发应用了三种新型耐酸性不锈钢波纹补偿器并逐步在莱钢热电厂应用，从目前的情况看，效果良 好。 2 波纹管膨胀节失效分析 2.1 波纹管膨胀节设计 波纹管膨胀节设计条件： 3 介质：高炉煤气；含尘量：≤12g/m ；运行压力＜0.25MPa ；温度：＜300℃；煤气流速：15～25m/s ； 2007 中国钢