降低CSP低碳钢成品酸溶铝含量生产实践.pdfVIP

降低CSP低碳铝镇静钢成品酸溶铝含量生产实践1 徐学良 王彦杰 唐志军 成旭东 （河北钢铁集团邯钢分公司三炼钢厂，邯郸 056000 ） 摘 要 为稳定 CSP 低碳铝镇静钢钢水质量，生产优质卷板及为冷轧提供优质原料，降低铝制品消耗及 CSP 低碳 铝镇静钢热轧板卷成品平均酸溶铝含量，三炼钢厂结合生产实际，采取一系列有效措施，优化转炉—精炼操作工艺， 经过生产实践，综合铝制品成本大幅降低，CSP 低碳铝镇静钢的成品酸溶铝含量由 0.0299%降至0.0260%以下。 关键词 CSP 低碳铝镇静钢 酸溶铝 Reduce the CSP Low Carbon Steel Product Aluminum Calm Acid Soluble Content of Aluminum Production Practice Xu Xueliang Wang Yanjie Tang Zhijun Cheng Xudong (No.3 Steelmaking Plant Handan Branch Hebei Iron and Steel Group, Handan, 056000) Abstract To stabilize the CSP low carbon steel, aluminum calm steel quality production high quality rolled plate and for cold rolled to provide high quality raw materials, reduce the aluminum consumption and CSP low carbon steel plate roll hot aluminum calm finished product acid soluble, aluminum content on average three steel mills, combination with the production practice, take a series of effective measures to optimize refining process, converter-through production practice, a much lower cost integrated aluminum, aluminum CSP low carbon steel finished product acid soluble calm aluminium content decreased from 0.0299% to less than 0.0260%. Key words CSP, Low carbon steel, aluminum calm Acid soluble aluminum 1 引言 酸溶铝主要指金属铝[Al]和氮化铝AlN ；酸不溶铝主要指氧化铝(Al O )，全铝主要指钢中的酸溶铝和氧 2 3 化铝(酸不溶铝)之和。铝是钢的重要合金元素之一，可以改善钢的延展性，由于铝在钢液中极易氧化，所以， CSP低碳铝镇钢中酸溶铝的控制是炼钢生产的一大难点。 在生产实践中各钢厂对钢中酸溶铝的控制存在着不同的意见。有的人认为钢中酸溶铝控制得越高越好， 因为现在连铸实行全程保护浇注，钢中溶解氧越低，铝的二次氧化少，并不产生水口堵塞，可浇性好。但随 着铝的加入量增加，带来生产成本的增加和连铸坯缺陷的增加[1] 。由于铝是强脱氧元素，因此铝的收得率相 当不稳定，钢中的酸溶铝也不稳定。 钢中酸溶铝控制过高时，造成铝制品的浪费；过低时，增加了 LF 精炼调铝的时间和精炼后期补加铝的 几率。为了提高和确保 CSP 低碳铝镇钢钢水质量，降低成品酸溶铝含量和生产成本，生产优质卷板及为冷 徐学良，男，本科，工程师，从事钢铁冶金