导电聚合物的温差电性能.pdfVIP

导电聚合物的温差电性能/刘显杰 ·27 · 导电聚合物的温差电性能 刘显杰 ( 中国船舶重工集团公司第712 所，武汉 430064) 摘要 人们应用塞贝克效应、帕尔帖效应和汤姆逊效应先后制造了各种温差电器件，如温差电发电器、温差电致 冷器、温差电传感器、温差电探测器等，而温差电材料是实现这些效应的关键，目前应用得最好的是块状半导体材料BiTe。 主要综述了目前在温差电领域研究的一些导电聚合物的研究进展，其中主要包括聚乙炔、聚苯胺、聚噻吩、聚吡咯等。 关键词 温差电材料 导电聚合物 聚乙炔 聚苯胺 聚噻吩 聚吡咯 Thermoelectric Properties of Conducting Polymers LIU Xianjie (The 712 Research Institute ,CSIC , Wuhan 430064) Abstract Seebeck effect，Peltier effect and Thomson effect are the foundation of the thermoelectrics ．According to these effects，many kinds of thermoelectric devices such as thermoelectric generators ，Peltier coolers ，thermoelectric sensors ，and thermoelectric detectors are eveloped .The material is the key to the thermoelectric devices, the most successful thermoelectrics to date have been made from ceramic materials, but there are few articles about organic meterials used as ther-moelectric material .In this paper, a number of organic conducting polymers are reviewed.for their thermoelectric properties, these include: polyacetylene, polyaniline, polythiophene, polypyrrole,et al. Key words hermoelectric ，conduting polymer ，polyacetylene polyaniline ，polypyrrole 单位为mV/K ，所有的温差电功率为正。尽管掺杂TaCl 的聚 0 引言 5 乙炔具有相当高的温差电功率，但它的电导率却很低，仅为 目前最成功的温差电材料是陶瓷类材料，比如BiTe。 0.06S/cm ，因此优值很小。对于这种物质来说，变量跳跃 但是，近20 年来这种材料的优值却只得到了很小的提高。 对于陶瓷材料而言，电导率的增加常常伴随着电子对热导率 (Variable range hopping,下同)机理可以很好地描述其对温度 的依存关系。对于拉伸样品，掺杂FeCl 的薄膜(5mm ×1m