溶融ガラスの超音波特性と流速計測に関する基礎研究.pdfVIP

溶融ガラスの超音波特性と流速計測に関する基礎研究 The Study of Ultrasound Characteristics and Velocimetry in Molten Glass. ○学 井原 智則（東工大） 正 木倉 宏成（東工大） 武田 靖 （東工大） 稲垣 彰 （日本原燃） 越智 英治（日本原燃） Tomonori IHARA, Hiroshige KIKURA, and Yasushi TAKEDA Tokyo Institute of Technology, 2-12-1, Ookayama, Meguro-ku, Tokyo Akira INAGAKI and Eiji OCHI Japan Nuclear Fuel Limited, 4-108 Okitsuke Obuchi, Rokkasho-mura, Kamikita, Aomori High temperature measurement system is presented. This system employs the ultrasonic buffer rod and pulsed Doppler method. The buffer rod has a cooling jacket to use the high efficiency room temperature transducer. For considering ultrasonic velocimetry method in the molten borosilicate glass, the temperature dependency of sound velocity at the temperature of 1000°C to 1200°C is obtained using cross-correlation technique, and its difference is within plus-minus 5%. A numerical simulation is also applied to design the optimised buffer rod, and its result shows good agreement with an experiment. Using this technique, the velocity, especially the speed of relative moving wall is obtained, and its error is within 3% when a value remained in measurable velocity. Key Words : High temperature, Ultrasound velocity, Velocimetry, Buffer rod, Molten glass １．はじめに 核燃料のリサイクル時に発生する高レベル放射性廃棄物 は，ガラス固化された後に地層処分されることが検討され ている．このガラス固化に用いられるガラス溶融炉では， 炉内の電極から溶融ガラスに直接通電を行うことで生じる ジュール熱によって，1000℃以上の温度に加熱される．こ うした中で，放射性廃棄物に含まれる導電率の高い白金族 元素の沈降や堆積挙動が溶融炉の安定運転を考える上で重 要となっている．そこで，高温の溶融ガラス内の流動を計 測するための手段が求められている． 流動計測の手法としては，熱線流速計やレーザドップラ 流速計，画像処理